Lubrizol ESTANE® GP75AE Ester Based Thermoplastic Polyurethane

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer	Lubrizol (former Noveon)
Trade Name	ESTANE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol ESTANE® GP75AE Ester Based Thermoplastic Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Type: Estane® GP 75AE is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided by Lubrizol.

Physical Properties	Metric	English	Comments
Specific Gravity	1.22 g/cc	1.22 g/cc	ISO 2781
Maximum Moisture Content	0.050	0.050
Melt Flow	5.0 - 15 g/10 min @Load 8.70 kg, Temperature 175 °C	5.0 - 15 g/10 min @Load 19.2 lb, Temperature 347 °F

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	75	75	ISO 868
Tensile Strength, Ultimate	30.0 MPa	4350 psi	ISO 37
Elongation at Break	800 %	800 %	ISO 37
Tensile Modulus	0.00600 GPa	0.870 ksi	ISO 527
50% Modulus	0.00300 GPa	0.435 ksi	ISO 37
100% Modulus	0.00400 GPa	0.580 ksi	ISO 37
300% Modulus	0.00700 GPa	1.02 ksi	ISO 37
Rebound	49 %	49 %	ISO 4662
Tear Strength	45.0 kN/m	257 pli	with incision; ISO 34B
	75.0 kN/m	428 pli	without incision; ISO 34B
Abrasion	25	25	mm<sup>3</sup>; ISO 4649
Compression Set	22 %	22 %	70 hrs./22°C; ISO 815
	40 %	40 %	24 hrs./70°C; ISO 815

Thermal Properties	Metric	English	Comments
Vicat Softening Point	82.0 °C	180 °F	A50; ISO 306

Processing Properties	Metric	English	Comments
Feed Temperature	40.0 °C	104 °F	Injection
Nozzle Temperature	>= 180 °C	>= 356 °F	Injection
Zone 1	175 - 185 °C	347 - 365 °F	Injection
Zone 2	180 - 190 °C	356 - 374 °F	Injection
Zone 3	185 - 195 °C	365 - 383 °F	Injection
Zone 4	185 - 195 °C	365 - 383 °F	Injection
Drying Temperature	80.0 °C	176 °F
Dry Time	2.00 - 3.00 hour	2.00 - 3.00 hour
Dew Point	-30.0 °C	-22.0 °F

Users viewing this material also viewed the following: