Lubrizol ESTANE® ETE50DT3 Ester Based Thermoplastic Polyurethane

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol ESTANE® ETE50DT3 Ester Based Thermoplastic Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Hard TPU with wide extrusion processing window and melt stability, low temperature flexibility, high transparency, UV stableUses: Extrusion: Hose and Tube, Profile, Cable Jacket; Injection molding: VariousAvailable in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by Lubrizol.
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Mechanical Properties Metric English Comments
Hardness, Shore D 47 - 53

@Time 5.00 sec
47 - 53

@Time 0.00139 hour
ASTM D2240
Tensile Strength 60.0 MPa
8700 psi
ASTM D412
Tensile Strength, Ultimate 46.8 MPa

@Temperature 70.0 °C,
Time 3.629e+6 sec
6790 psi

@Temperature 158 °F,
Time 1008 hour
Water Immersion
46.8 MPa

@Temperature 100 °C,
Time 2.42e+6 sec
6790 psi

@Temperature 212 °F,
Time 672 hour
Oven Aging
48.0 MPa

@Temperature 70.0 °C,
Time 1.21e+6 sec
6960 psi

@Temperature 158 °F,
Time 336 hour
Water Immersion
48.0 MPa

@Temperature 70.0 °C,
Time 2.42e+6 sec
6960 psi

@Temperature 158 °F,
Time 672 hour
Water Immersion
49.2 MPa

@Temperature 100 °C,
Time 605000 sec
7140 psi

@Temperature 212 °F,
Time 168 hour
Oven Aging
60.0 MPa

@Temperature 70.0 °C,
Time 0.000 sec
8700 psi

@Temperature 158 °F,
Time 0.000 hour
Water Immersion
60.0 MPa

@Temperature 100 °C,
Time 0.000 sec
8700 psi

@Temperature 212 °F,
Time 0.000 hour
Oven Aging
Elongation at Break 410 %
410 %
ASTM D412
100% Modulus 0.0152 GPa
2.20 ksi
ASTM D412
300% Modulus 0.0352 GPa
5.11 ksi
ASTM D412
Tear Strength 33.3 kN/m
190 pli
Trousers; ASTM D470
Graves Tear Strength 142 kN/m
810 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 81
81
H18, 1000g; ASTM D3389 B
Thermal Properties Metric English Comments
Melting Point 150 °C
302 °F
DSC
Glass Transition Temp, Tg -33.0 °C
-27.4 °F
DSC
Processing Properties Metric English Comments
Zone 1 193 °C
379 °F
Extrusion
Zone 2 199 °C
390 °F
Extrusion
Zone 3 204 °C
399 °F
Extrusion
Zone 4 210 °C
410 °F
Extrusion
Adapter Temperature 210 °C
410 °F
5, Extrusion
Die Temperature 210 °C
410 °F
6, Zone 1, Extrusion
210 °C
410 °F
Zone 2, Extrusion
Drying Temperature 104 °C
219 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Dew Point -40.0 °C
-40.0 °F