Lubrizol ESTANE® 58315 Ether Based Thermoplastic Polyurethane

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol ESTANE® 58315 Ether Based Thermoplastic Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Very good physical properties, hydrolysis resistance, low temperature performance and abrasion. Wide processing window for extrusion.Uses: Blown and flat die/cast film extrusion, Injection molding and cable jacketing.Available in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by Lubrizol.
Physical Properties Metric English Comments
Specific Gravity 1.12 g/cc
1.12 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Mechanical Properties Metric English Comments
Hardness, Shore A 82 - 88

@Time 5.00 sec
82 - 88

@Time 0.00139 hour
ASTM D2240
Tensile Strength 48.3 MPa
7010 psi
ASTM D412
33.81 MPa

@Temperature 75.0 °C,
Time 4.838e+6 sec
4904 psi

@Temperature 167 °F,
Time 1344 hour
30 Mil Sheet, Immersion in Water
39.12 MPa

@Temperature 75.0 °C,
Time 605000 sec
5674 psi

@Temperature 167 °F,
Time 168 hour
30 Mil Sheet, Immersion in Water
39.12 MPa

@Temperature 75.0 °C,
Time 1.21e+6 sec
5674 psi

@Temperature 167 °F,
Time 336 hour
30 Mil Sheet, Immersion in Water
46.85 MPa

@Temperature 75.0 °C,
Time 2.82e+6 sec
6795 psi

@Temperature 167 °F,
Time 784 hour
30 Mil Sheet, Immersion in Water
48.3 MPa

@Temperature 75.0 °C,
Time 0.000 sec
7010 psi

@Temperature 167 °F,
Time 0.000 hour
30 Mil Sheet, Immersion in Water
Elongation at Break 570 %
570 %
ASTM D412
100% Modulus 0.00620 GPa
0.899 ksi
ASTM D412
300% Modulus 0.0103 GPa
1.49 ksi
ASTM D412
Tear Strength 26.3 kN/m
150 pli
Trosuer; ASTM D470
Graves Tear Strength 85.9 kN/m
490 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 37
37
H18, 1000g; ASTM D3389 B
Tensile Set 14 %
14 %
200% elongation; ASTM D412
Thermal Properties Metric English Comments
Melting Point 135 °C
275 °F
DSC
145 °C
293 °F
Kofler
Glass Transition Temp, Tg -50.0 °C
-58.0 °F
DSC
Optical Properties Metric English Comments
Haze 1.8 %
1.8 %
pressed between glass; ASTM D1003
Processing Properties Metric English Comments
Zone 1 171 °C
340 °F
Extrusion
Zone 2 177 °C
351 °F
Extrusion
Zone 3 182 °C
360 °F
Extrusion
Zone 4 188 °C
370 °F
Extrusion
Adapter Temperature 188 °C
370 °F
5, Extrusion
Die Temperature 188 °C
370 °F
6, Zone 1, Extrusion
188 °C
370 °F
Zone 2, Extrusion
Drying Temperature 104 °C
219 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Dew Point -40.0 °C
-40.0 °F