Lubrizol ESTANE® 58309 Ether Based Thermoplastic Polyurethane

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol ESTANE® 58309 Ether Based Thermoplastic Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Good Physical Properties and Reduced Surface Tack.Uses: Flat Die/Cast Film and Blown Film Extrusion, Injection MoldingAvailable in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by Lubrizol.
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Linear Mold Shrinkage 0.0014 cm/cm
0.0014 in/in
Injection
Mechanical Properties Metric English Comments
Hardness, Shore A 82 - 88

@Time 5.00 sec
82 - 88

@Time 0.00139 hour
ASTM D2240
Tensile Strength 44.8 MPa
6500 psi
ASTM D412
Elongation at Break 570 %
570 %
ASTM D412
100% Modulus 0.00620 GPa
0.899 ksi
ASTM D412
300% Modulus 0.0110 GPa
1.60 ksi
ASTM D412
Flexural Modulus 0.0290 GPa
4.20 ksi
ASTM D790
Tear Strength 22.8 kN/m
130 pli
Trouser; ASTM D470
Graves Tear Strength 78.9 kN/m
450 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 21
21
H18, 1000g; ASTM D3389 B
Tensile Set 19 %
19 %
200% elongation; ASTM D412/D638
Thermal Properties Metric English Comments
Melting Point 135 °C
275 °F
145 °C
293 °F
Kofler
Glass Transition Temp, Tg -46.0 °C
-50.8 °F
Processing Properties Metric English Comments
Rear Barrel Temperature 193 °C
379 °F
Injection
Middle Barrel Temperature 204 °C
399 °F
Injection
Front Barrel Temperature 216 °C
421 °F
Injection
Nozzle Temperature 216 °C
421 °F
Injection
Zone 1 176 °C
349 °F
Extrusion
Zone 2 183 °C
361 °F
Extrusion
Zone 3 188 °C
370 °F
Extrusion
Zone 4 194 °C
381 °F
Extrusion
Adapter Temperature 194 °C
381 °F
Extrusion
Die Temperature 194 °C
381 °F
Zone 1, Extrusion
194 °C
381 °F
Zone 2, Extrusion
Melt Temperature 216 °C
421 °F
Injection
Drying Temperature 104 °C
219 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Dew Point -40.0 °C
-40.0 °F
Injection Pressure 3000 - 7000 MPa
435000 - 1.02e+6 psi
Injection
Back Pressure 50.0 MPa
7250 psi
Injection
Screw Speed 20 - 50 rpm
20 - 50 rpm
Injection
Descriptive Properties Value Comments
Volume Swell in Water 1.7%
24h/23°C, ASTM D471