Lubrizol ESTANE® 58277 Ester Based Thermoplastic Polyurethane

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer	Lubrizol (former Noveon)
Trade Name	ESTANE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol ESTANE® 58277 Ester Based Thermoplastic Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Excellent physical properties, good chemical resistance and wide processing window for extrusion.Uses: Blown and flat die/cast film extrusion and Injection and blow molding.Complies with: FDA 177.1680 and FDA 177.2600Available in Americas, Europe, Middle East, Africa, India and AsiaInformation provided by Lubrizol

Physical Properties	Metric	English	Comments
Specific Gravity	1.22 g/cc	1.22 g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	89 - 95 @Time 5.00 sec	89 - 95 @Time 0.00139 hour	ASTM D2240
Tensile Strength	62.1 MPa	9010 psi	ASTM D412
	62.1 MPa @Temperature 23.0 °C, Time 0.000 sec	9010 psi @Temperature 73.4 °F, Time 0.000 hour	Thirty mil sheet immersion
	63.96 MPa @Temperature 23.0 °C, Time 1.30e+6 sec	9277 psi @Temperature 73.4 °F, Time 360 hour	Thirty mil sheet immersion
	65.02 MPa @Temperature 23.0 °C, Time 2.42e+6 sec	9430 psi @Temperature 73.4 °F, Time 672 hour	Thirty mil sheet immersion
	65.02 MPa @Temperature 23.0 °C, Time 5.011e+6 sec	9430 psi @Temperature 73.4 °F, Time 1392 hour	Thirty mil sheet immersion
Elongation at Break	450 %	450 %	ASTM D412
100% Modulus	0.00970 GPa	1.41 ksi	ASTM D412
300% Modulus	0.0290 GPa	4.21 ksi	ASTM D412
Tear Strength	33.3 kN/m	190 pli	Trouser; ASTM D470
Graves Tear Strength	114 kN/m	650 pli	Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles	2.6	2.6	H18, 1000g; ASTM D3389 B
Tensile Set	17 %	17 %	200% elongation; ASTM D412

Thermal Properties	Metric	English	Comments
Melting Point	130 °C	266 °F
	140 °C	284 °F	Kofler
Glass Transition Temp, Tg	-20.0 °C	-4.00 °F

Optical Properties	Metric	English	Comments
Haze	1.1 %	1.1 %	65 mil between glass; ASTM D1003

Processing Properties	Metric	English	Comments
Zone 1	177 °C	351 °F	Extrusion
Zone 2	182 °C	360 °F	Extrusion
Zone 3	188 °C	370 °F	Extrusion
Zone 4	193 °C	379 °F	Extrusion
Adapter Temperature	199 °C	390 °F	5, Extrusion
Die Temperature	199 °C	390 °F	Zone 1, Extrusion
	199 °C	390 °F	Zone 2, Extrusion
Drying Temperature	104 °C	219 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour
Dew Point	-40.0 °C	-40.0 °F

Descriptive Properties	Value	Comments
Volume Swell in Ethanol	12%	24 h, ASTM D471