Lubrizol ESTANE® 58133 Ester Based Thermoplastic Polyurethane

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol ESTANE® 58133 Ester Based Thermoplastic Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Fast cycling, broad temperature performance, and durabilityUse: Injection MoldingAvailable in Americas, Europe, Middle East, Africa, India and Asia Information provided by Lubrizol.
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
flex bar
0.013 cm/cm
0.013 in/in
disk
Mechanical Properties Metric English Comments
Hardness, Shore D 52 - 58

@Time 5.00 sec
52 - 58

@Time 0.00139 hour
ASTM D2240
Tensile Strength 41.0 MPa
5950 psi
ASTM D412
Elongation at Break 500 %
500 %
ASTM D412
100% Modulus 0.0150 GPa
2.18 ksi
ASTM D412
300% Modulus 0.0270 GPa
3.92 ksi
ASTM D412
Flexural Modulus 0.159 GPa
23.0 ksi
ASTM D790
Tear Strength 42.1 kN/m
240 pli
Trouser; ASTM D470
Graves Tear Strength 158 kN/m
900 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 34
34
CS-17, 1000g; ASTM D3389 B
Compression Set 37 %

@Temperature 23.0 °C,
Time 79200 sec
37 %

@Temperature 73.4 °F,
Time 22.0 hour
ASTM D395
49 %

@Temperature 70.0 °C,
Time 79200 sec
49 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D395
Thermal Properties Metric English Comments
Melting Point 221 °C
430 °F
DSC
Glass Transition Temp, Tg -30.0 °C
-22.0 °F
DSC
Processing Properties Metric English Comments
Rear Barrel Temperature 210 °C
410 °F
Injection
Middle Barrel Temperature 215 °C
419 °F
Injection
Front Barrel Temperature 224 °C
435 °F
Injection
Nozzle Temperature 229 °C
444 °F
Injection
Melt Temperature 229 °C
444 °F
Injection
Drying Temperature 104 °C
219 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Dew Point -40.0 °C
-40.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Injection
Hold Pressure 34.5 - 68.9 MPa
5000 - 10000 psi
Injection
Back Pressure >= 0.345 MPa
>= 50.0 psi
Injection
Screw Speed 60 - 100 rpm
60 - 100 rpm
Injection