Lubrizol Advanced Materials PEARLTHANE® 11H94 Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Lubrizol Advanced Materials Manufacturing S. S.L. (Former Merquinsa) |
| Trade Name | Pearlthane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials PEARLTHANE® 11H94 Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PEARLTHANE® D11H94 is a high performance polycaprolactone copolyester based TPU, supplied in form of translucent, colorless pellets, featuring adequate hardness as well as excellent flow and mechanical properties, including an outstandingly low compression set value. Product recommended for injection molding applications with an extremely short cycle time. PEARLTHANE® D11H94 is especially recommended for injection molding applications such as: automotive parts, seals and gaskets and a variety of high performance technical parts.All information provided by Merquinsa
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 21.6 kg |
10 g/10 min @Load 47.6 lb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Tensile Strength, Yield | 42.07 MPa | 6102 psi | ASTM D412 |
| Elongation at Break | 515 % | 515 % | ASTM D412 |
| 100% Modulus | 0.01202 GPa | 1.743 ksi | ASTM D412 |
| 300% Modulus | 0.02304 GPa | 3.341 ksi | ASTM D412 |
| Tear Strength | 135 kN/m | 771 pli | ASTM D624 (Die C) |
| Abrasion | 35 | 35 | loss (mm³); DIN 53.516 |
| Compression Set | 32 % @Temperature 70.0 °C, Time 79200 sec |
32 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 |
| 37 % @Temperature 70.0 °C, Time 252000 sec |
37 % @Temperature 158 °F, Time 70.0 hour |
ASTM D395 | |
| 43 % @Temperature 100 °C, Time 79200 sec |
43 % @Temperature 212 °F, Time 22.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 197 - 207 °C | 386 - 404 °F | MQSA 111 |
| Glass Transition Temp, Tg | -38.9 °C | -38.0 °F | DSC, 10ºC/min; DIN 51.007 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 210 °C | 410 °F | |
| Nozzle Temperature | 225 °C | 437 °F | |
| Zone 1 | 215 °C | 419 °F | Compression Zone |
| Zone 2 | 225 °C | 437 °F | Metering Zone |
| Mold Temperature | 40.0 °C | 104 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % | MQSA 44 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible 82024 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Loxim 300 00V0 Nylon 6
- Ineos ABS Lustran® Ultra 4000 PG ABS Pellets (a-methylstyrene-SAN-modified), Electroplating Grade
- SABIC Innovative Plastics LNP LUBRICOMP WL003 PBT (Europe-Africa-Middle East)
- Solvay Specialty Polymers Cogegum® AFR/765-UV Polyolefin
- SABIC Innovative Plastics Valox® IQ357 PBT+PC
- Unifrax Insulfrax® 1100C Modules
- Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 10% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved