Loxim 830 02C HB Polypropylene Compound, 30% Calcite Filled, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Calcium Carbonate (CaCO3) Filler , Polypropylene, Flame Retardant |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 830 02C HB Polypropylene Compound, 30% Calcite Filled, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 - 1.15 g/cc | 1.05 - 1.15 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage | 0.013 - 0.015 cm/cm | 0.013 - 0.015 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 26.0 - 28.0 MPa | 3770 - 4060 psi | ASTM D683 |
| Flexural Modulus | 1.80 - 2.00 GPa | 261 - 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.250 - 0.350 J/cm | 0.468 - 0.656 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 - 115 °C | 230 - 239 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |