Lotte Chemical Titan TITANEX® LF0754 Linear low density polyethylene Hexene-1 resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lotte Chemical Titan TITANEX® LF0754 Linear low density polyethylene Hexene-1 resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LF0754 is a pelleted linear low density polyethylene Hexene-1 resin formulated with antioxidant agent. This product is used for blown film extrusion which offers outstanding toughness, extrudability and draw down ability.Applications: Heavy duty shipping sacks, rice bags, ice bags, produce bags, stretch film, courier bags, multilayer film.Advantages: Excellent puncture strength, impact strength and tear strength.Information provided by Titan Chemicals

Physical Properties	Metric	English	Comments
Base Resin Density	0.920 g/cc	0.0332 lb/in³	ASTM D1505
Thickness	50.0 microns	1.97 mil	extruded at 2:1 BUR
Base Resin Melt Index	0.70 g/10 min	0.70 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	500 %	500 %	ASTM D882
Film Elongation at Break, TD	700 %	700 %	ASTM D882
Elmendorf Tear Strength, MD	18.0 g/micron	457 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	29.0 g/micron	737 g/mil	ASTM D1922
Dart Drop	9.00 g/micron	229 g/mil	ASTM D1709
Film Tensile Strength at Break, MD	39.2 MPa	5690 psi	ASTM D882
Film Tensile Strength at Break, TD	29.4 MPa	4260 psi	ASTM D882
1% Secant Modulus, MD	196.14 MPa	28447 psi	ASTM D882
1% Secant Modulus, TD	245.16 MPa	35558 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	10 %	10 %	ASTM D1003
Gloss	30 %	30 %	45°; ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	180 - 210 °C	356 - 410 °F
Blow-up Ratio (BUR)	2.0 - 3.0	2.0 - 3.0