Lord Adhesives Chemglaze® V209 Polyurethane Coating

Category Polymer , Thermoset , Polyurethane, TS
Manufacturer Lord Adhesives
Trade Name Chemglaze®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lord Adhesives Chemglaze® V209 Polyurethane Coating.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Chemglaze® V-Line polyurethane coatings are moisture curing aliphatic polyurethane coatings. They are used in product finishing applications on polyvinyl-chloride (PVC) and other plastics where maximum performance properties are needed. These coatings provide the highest possible combinations of abrasion resistance, wear properties and flexibility. Use Chemglaze V-Line coatings as protective coatings for vinyl, Mylar®, ABS, FRP, and Noryl®.Excellent wear is characteristic of all Chemglaze products. In laboratory evaluations 7.6 to 38.1 µm (0.3 to 1.5 mils) of Chemglaze V-Line polyurethane coatings provide better scuff and wear resistance than 50.8 - 76.2 µm (2 to 3 mils) of conventional scuff coats.Flexible GlossAll information provided by Lord.
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
ASTM D1475
Solids Content 37.2 %
37.2 %
by volume; ASTM D2369 Modified
49.5 %
49.5 %
by weight; ASTM D2369 Modified
Volatile Organic Compounds (VOC) Content 550 g/l
550 g/l
ASTM D3960
Brookfield Viscosity 450 cP
450 cP
ASTM D2196, LVT, Spindle #2 @ 30rpm
Mechanical Properties Metric English Comments
Tensile Strength, Yield 27.6 MPa
4000 psi
Coatings catalyzed 2% with 9995, baked 15 minutes @ 107ºC, post cured 2 weeks @ 25ºC and 50% relative humidity. Free films tested on an Instron tester
Elongation at Yield 250 %
250 %
Coatings catalyzed 2% with 9995, baked 15 minutes @ 107ºC, post cured 2 weeks @ 25ºC and 50% relative humidity. Free films tested on an Instron tester
Thermal Properties Metric English Comments
Flash Point 20.0 °C
68.0 °F
ASTM D3278, Seta Flash, Closed Cup
Processing Properties Metric English Comments
Cure Time 1.00 - 4.00 min

@Temperature 149 - 191 °C
0.0167 - 0.0667 hour

@Temperature 300 - 376 °F
2.00 - 5.00 min

@Temperature 121 - 149 °C
0.0333 - 0.0833 hour

@Temperature 250 - 300 °F
10.0 - 30.0 min

@Temperature 93.0 - 121 °C
0.167 - 0.500 hour

@Temperature 199 - 250 °F
Descriptive Properties Value Comments
Appearance White
Theoretical Coverage (ft²/gallon/mil) 595