Lord Adhesives Aeroglaze® 9744 Epoxy Primer/Tie-Coat
| Category | Polymer , Thermoset , Epoxy |
| Manufacturer | Lord Adhesives |
| Trade Name | Aeroglaze® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lord Adhesives Aeroglaze® 9744 Epoxy Primer/Tie-Coat.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aeroglaze® 9744 is a two-part epoxy primer designed for use on aluminum, metal, and prepared composite surfaces. Aeroglaze 9744 primer/tie-coat is applied to scuff-sanded urethane top coats and epoxy primers. It is also used as a tie-coat between scuff-sanded weather worn coatings and new urethane topcoats.All information provided by Lord.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | 9700B |
| 1.33 g/cc | 0.0480 lb/in³ | Mixed | |
| 1.47 g/cc | 0.0531 lb/in³ | 9744A | |
| Solids Content | 59.9 % | 59.9 % | 9744A; by volume; ASTM D3278-82 |
| 64.4 % | 64.4 % | Mixed, by volume; ASTM D3278-82 | |
| 76 % | 76 % | 9744A; by weight; ASTM D3278-82 | |
| 76.8 % | 76.8 % | Mixed, by weight; ASTM D3278-82 | |
| 77.8 % | 77.8 % | 9700B, by volume; ASTM D3278-82 | |
| 80.3 % | 80.3 % | 9700B, by weight; ASTM D3278-82 | |
| Volatile Organic Compounds (VOC) Content | 180 g/l | 180 g/l | 9700B; ASTM D3960-89 |
| 308.2 g/l | 308.2 g/l | Mixed; ASTM D3960-89 | |
| 350.91 g/l | 350.91 g/l | 9744A; ASTM D3960-89 | |
| Viscosity Measurement | <= 31 @Temperature 25.0 °C |
<= 31 @Temperature 77.0 °F |
944A; #4 Ford Cup (seconds); ASTM D1200 |
| <= 40 @Temperature 25.0 °C |
<= 40 @Temperature 77.0 °F |
Mixed; #4 Ford Cup (seconds); ASTM D1200 | |
| 61 @Temperature 25.0 °C |
61 @Temperature 77.0 °F |
9700B; #4 Ford Cup (seconds); ASTM D1200 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flash Point | >= 21.7 °C | >= 71.1 °F | 9744A; Setaflash, Closed Cup; ASTM D3278-82 |
| >= 26.3 °C | >= 79.3 °F | 9700B; Setaflash, Closed Cup; ASTM D3278-82 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | >= 300 min @Temperature 25.0 °C |
>= 5.00 hour @Temperature 77.0 °F |
|
| Pot Life | 240 min @Temperature 25.0 °C |
240 min @Temperature 77.0 °F |
|
| Shelf Life | 6.00 Month @Temperature 21.0 - 27.0 °C |
6.00 Month @Temperature 69.8 - 80.6 °F |
9744A |
| 6.00 Month @Temperature 21.0 - 27.0 °C |
6.00 Month @Temperature 69.8 - 80.6 °F |
9700B |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear Amber | 9700B |
| Dark Gray | Mixed | |
| Dark Gray | 9744A | |
| Coating Film Dry Weight (gm/ft²/mil) | 3.73 | |
| Theoretical Coverage (ft²/gallon/mil) | 1033 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® ES-40GF/000 Polyethersulfone - 40% Glass Fiber Reinforced (discontinued **)
- Premix Thermoplastics PRE-ELEC® PE 1304 (discontinued **)
- MarkeTech Zirconium Oxide Ceramic - Zirconia, Y2O3 Stabilized
- DSM Somos® Precise Stereolithography Polymer
- Diamond Polymers Softflex® 8200
- AlphaGary Evoprene™ GC 5701 SEBS Thermoplastic Elastomer
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 316°C Temper
- BASF Pluracol® 726 Specialty Polyol
- SABIC Innovative Plastics LNP THERMOCOMP RF0069XZ PA 66 (Asia Pacific)
- SABIC Innovative Plastics LNP VERTON RV00CEXS PA 66
Copyright © lookpolymers.com All Rights Reserved