Lehmann & Voss LUVOCOMÂ® 94-8485 LD-PE, unreinforced

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Lehmann & Voss & Co.
Trade Name	LUVOCOM®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lehmann & Voss LUVOCOMÂ® 94-8485 LD-PE, unreinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Reduced moment of inertia compared with metal parts.Dynamic stressed parts.Especially suitable for thin wall complex parts.Information provided by Lehmann & Voss & Co.KG

Physical Properties	Metric	English	Comments
Specific Gravity	1.57 g/cc	1.57 g/cc	ISO 1183
Water Absorption	<= 0.10 %	<= 0.10 %	23Â°C/24h
Linear Mold Shrinkage	0.015 - 0.030 cm/cm	0.015 - 0.030 in/in
Melt Flow	>= 50 g/10 min @Load 2.16 kg, Temperature 190 Â°C	>= 50 g/10 min @Load 4.76 lb, Temperature 374 Â°F

Mechanical Properties	Metric	English	Comments
Tensile Stress	9.00 MPa	1310 psi
Elongation at Yield	20 %	20 %
Modulus of Elasticity	0.300 GPa	43.5 ksi
Charpy Impact Unnotched	NB	NB	flatwise; ISO 179 1fU
	NB @Temperature -30.0 Â°C	NB @Temperature -22.0 Â°F	ISO 179

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	70.0 Â°C	158 Â°F
	100 Â°C	212 Â°F	short term
Vicat Softening Point	80.0 Â°C	176 Â°F	DIN ISO 306

Electrical Properties	Metric	English	Comments
Surface Resistance	>= 1.00e+9 ohm	>= 1.00e+9 ohm
Insulation Resistance	>= 1.00e+9 ohm	>= 1.00e+9 ohm

Processing Properties	Metric	English	Comments
Processing Temperature	230 Â°C	446 Â°F	mass temp
Nozzle Temperature	190 - 250 Â°C	374 - 482 Â°F
Zone 1	160 - 200 Â°C	320 - 392 Â°F
Zone 2	170 - 220 Â°C	338 - 428 Â°F
Zone 3	180 - 240 Â°C	356 - 464 Â°F
Mold Temperature	30.0 - 80.0 Â°C	86.0 - 176 Â°F
Drying Temperature	85.0 Â°C @Time 7200 - 10800 sec	185 Â°F @Time 2.00 - 3.00 hour	Dehumidifying dryer

Descriptive Properties	Value	Comments
Color	natural color (black)