Lehmann & Voss LUVOCOM® 7-0755 Polyamide 610, with glass fiber and PTFE

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer Lehmann & Voss & Co.
Trade Name LUVOCOM®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lehmann & Voss LUVOCOM® 7-0755 Polyamide 610, with glass fiber and PTFE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and stiff parts; low coefficient of expansion.Improved friction and wear behaviour. Emergency running property.Reduced waterabsorbtion.High dimensionally stable precision parts.Bearings, sleeves, sliding elements, handles, machine parts.Information provided by Lehmann & Voss & Co.KG
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
ISO 1183
Water Absorption <= 0.15 %
<= 0.15 %
23°C/24h
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
Mechanical Properties Metric English Comments
Tensile Stress 200 MPa
29000 psi
Elongation at Yield 3.5 %
3.5 %
4.0 %
4.0 %
flexural
Modulus of Elasticity 11.0 GPa
1600 ksi
Flexural Strength 290 MPa
42100 psi
Flexural Modulus 9.00 GPa
1310 ksi
Charpy Impact Unnotched 10.0 J/cm²
47.6 ft-lb/in²
edgewise; ISO 179 1eU
8.50 J/cm²

@Temperature -30.0 °C
40.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Coefficient of Friction, Dynamic 0.35
0.35
Coefficient of Friction, Static 0.25
0.25
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C
22.2 µin/in-°F
DIN 53752
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
DIN 52612
Maximum Service Temperature, Air 90.0 °C
194 °F
140 °C
284 °F
short term
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Electrical Properties Metric English Comments
Insulation Resistance >= 1.00e+12 ohm
>= 1.00e+12 ohm
Processing Properties Metric English Comments
Processing Temperature 265 °C
509 °F
mass temp
Nozzle Temperature 270 - 290 °C
518 - 554 °F
Zone 1 240 - 270 °C
464 - 518 °F
Zone 2 260 - 280 °C
500 - 536 °F
Zone 3 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 75.0 °C

@Time 21600 - 36000 sec
167 °F

@Time 6.00 - 10.0 hour
Dehumidifying dryer
105 °C

@Time <=14400 sec
221 °F

@Time <=4.00 hour
or
Descriptive Properties Value Comments
Color natural color (beige)