- Lehmann & Voss LUVOCOM® 6-8211 Polyamide 12, with glass fiber, thermally conductive modified
Lehmann & Voss LUVOCOM® 6-8211 Polyamide 12, with glass fiber, thermally conductive modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 20% Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 6-8211 Polyamide 12, with glass fiber, thermally conductive modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Especially suitable at dynamic stress situations.Low waterabsorbtion, for dimensional stable precision parts.Bearings, sleeves, sliding elements, chair rollers, handles.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 105 MPa | 15200 psi | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| 3.8 % | 3.8 % | flexural | |
| Modulus of Elasticity | 8.60 GPa | 1250 ksi | |
| Flexural Strength | 165 MPa | 23900 psi | |
| Flexural Modulus | 7.50 GPa | 1090 ksi | |
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.50 W/m-K | 10.4 BTU-in/hr-ft²-°F | HOT-DISK || 60x60x3 mm |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 140 °C | 284 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |
| Zone 2 | 240 - 260 °C | 464 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec |
167 °F @Time 6.00 - 10.0 hour |
Dehumidifying dryer |
| 105 °C @Time <=14400 sec |
221 °F @Time <=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | graphite grey |
Users viewing this material also viewed the following:
- Pyrotek SF-50 Foamed Fused Silica Insulation Board
- DuPont™ Clysar® EHC Polyolefin Shrink Packaging Film, 75 Gauge (discontinued **)
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 8 PHR Di-Cup 40C
- Huntsman AVALON® 65 AK-ESD Thermoplastic Polyurethane
- Gouda Vuurvast CURON 150 Dense Refractory Castable
- Shin-Etsu Silicones Wetter No. 5 Silicone Fluid
- Sumitomo Bakelite North America Epiall® 1908-1 Short Glass Fiber Reinforced Epoxy
- Teknor Apex TruVis Esters™ DTDA Di-Tridecyl Adipate
- Dow Nordel® IP 4725P EPDM Hydrocarbon Rubber
- 3M 396 Super Bond Film
Copyright © lookpolymers.com All Rights Reserved