Lehmann & Voss LUVOCOM® 3-8363 Polyamide 6, unreinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 3-8363 Polyamide 6, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Reduced moment of inertia compared with metal parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.013 - 0.018 cm/cm | 0.013 - 0.018 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 60.0 MPa | 8700 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 3.0 % | 3.0 % | flexural | |
| Modulus of Elasticity | 4.40 GPa | 638 ksi | |
| Flexural Strength | 85.0 MPa | 12300 psi | |
| Flexural Modulus | 3.90 GPa | 566 ksi | |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| 120 °C | 248 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm | |
| Insulation Resistance | >= 1.00e+10 ohm | >= 1.00e+10 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 °C | 518 °F | mass temp |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | |
| Zone 1 | 250 - 270 °C | 482 - 518 °F | |
| Zone 2 | 270 - 290 °C | 518 - 554 °F | |
| Zone 3 | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 36000 - 57600 sec |
167 °F @Time 10.0 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | red |
Users viewing this material also viewed the following:
- Ineos Nova 3601 General Purpose Crystal Polystyrene (discontinued **)
- Mateck Fused Silica UV-VIS Grade (SiO2)
- SABIC Innovative Plastics LNP LUBRICOMP ZFL31XXC PPE+PS
- A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene
- Covestro Makrolon® 6557 Polycarbonate, Injection Grade
- E-Polymers SEPAZ® LH50 PP Homopolymer LFT Resin
- BASF Neopor® 2400 Expandable Polystyrene
- Technetics Group Texolon™ 8534 PTFE (Unverified Data**)
- Chevron Phillips K-Resin® DK13 Styrene-Butadiene Copolymer, Film Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved