Lehmann & Voss LUVOCOM® 2211-7726 Blend of polyarylate, with carbon fiber

Category Polymer , Thermoplastic , Polyarylate
Manufacturer Lehmann & Voss & Co.
Trade Name LUVOCOM®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lehmann & Voss LUVOCOM® 2211-7726 Blend of polyarylate, with carbon fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Strong, stiff parts.High continuous use and heat distortion temperature. Non flammable.High dimensionally stable precision parts.Suitable for discharging of statically generated electricity.Transporting equipment for electrically sensible goods.Information provided by Lehmann & Voss & Co.KG
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ISO 1183
Water Absorption <= 0.20 %
<= 0.20 %
23°C/24h
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Mechanical Properties Metric English Comments
Tensile Stress 165 MPa
23900 psi
Elongation at Yield 3.0 %
3.0 %
4.0 %
4.0 %
flexural
Modulus of Elasticity 13.0 GPa
1890 ksi
Flexural Strength 240 MPa
34800 psi
Flexural Modulus 11.0 GPa
1600 ksi
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
edgewise; ISO 179 1eU
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179 1eA
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 220 °C
428 °F
250 °C
482 °F
short term
Electrical Properties Metric English Comments
Insulation Resistance <= 1.00e+6 ohm
<= 1.00e+6 ohm
Processing Properties Metric English Comments
Processing Temperature 390 °C
734 °F
mass temp
Nozzle Temperature 360 - 380 °C
680 - 716 °F
Zone 1 360 - 370 °C
680 - 698 °F
Zone 2 370 - 380 °C
698 - 716 °F
Zone 3 380 - 390 °C
716 - 734 °F
Mold Temperature 160 - 200 °C
320 - 392 °F
Drying Temperature 120 - 150 °C

@Time >=10800 sec
248 - 302 °F

@Time >=3.00 hour
Dehumidifying dryer
Descriptive Properties Value Comments
Color natural color (black)