- Lehmann & Voss LUVOCOM® 20-8302 Polyphthalamide, with carbon fiber, PTFE, lubricant modified
Lehmann & Voss LUVOCOM® 20-8302 Polyphthalamide, with carbon fiber, PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Carbon Fiber + PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 20-8302 Polyphthalamide, with carbon fiber, PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Low influence from moisture and temperature to measures and electrical properties, compared with PA66Suitable for metall inserts.Improved friction and wear behaviour. Emergency running property.Bearings, sleeves, sliding elements, control disks, gear wheels, duty parts in switches.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0030 cm/cm | 0.00050 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 260 MPa | 37700 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 1.9 % | 1.9 % | flexural | |
| Modulus of Elasticity | 26.0 GPa | 3770 ksi | |
| Flexural Strength | 370 MPa | 53700 psi | |
| Flexural Modulus | 21.0 GPa | 3050 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| 195 °C | 383 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 330 °C | 608 - 626 °F | |
| Zone 1 | 320 - 340 °C | 608 - 644 °F | |
| Zone 2 | 320 - 345 °C | 608 - 653 °F | |
| Zone 3 | 325 - 350 °C | 617 - 662 °F | |
| Mold Temperature | 135 - 160 °C | 275 - 320 °F | |
| Drying Temperature | 80.0 °C @Time 57600 sec |
176 °F @Time 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 18000 sec |
221 °F @Time 4.00 - 5.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |