Lehmann & Voss LUVOCOM® 20-8244 Polyphthalamide, with carbon fiber and glass fiber
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 20-8244 Polyphthalamide, with carbon fiber and glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 115 MPa | 16700 psi | |
| Elongation at Yield | 1.2 % | 1.2 % | |
| 1.8 % | 1.8 % | flexural | |
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | |
| Flexural Strength | 180 MPa | 26100 psi | |
| Flexural Modulus | 10.0 GPa | 1450 ksi | |
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | edgewise; ISO 179 1eU |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| 195 °C | 383 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
| Insulation Resistance | 10000 - 1.00e+8 ohm | 10000 - 1.00e+8 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 330 °C | 608 - 626 °F | |
| Zone 1 | 320 - 340 °C | 608 - 644 °F | |
| Zone 2 | 320 - 345 °C | 608 - 653 °F | |
| Zone 3 | 325 - 350 °C | 617 - 662 °F | |
| Mold Temperature | 135 - 160 °C | 275 - 320 °F | |
| Drying Temperature | 80.0 °C @Time 57600 sec |
176 °F @Time 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 18000 sec |
221 °F @Time 4.00 - 5.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Plaskolite Optix® CP - 51 KC General Purpose Acrylic Resin
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 285ºF Cure Temperature
- LyondellBasell Montell 16502F7 Butene LLDPE
- Inhance Fluoro-Seal INHANCE® UH-1045 Ultra High Molecular Weight Polyethylene
- Lucite International Perspexâ„¢ XT IM60 Acrylic Impact Modified Extruded Sheet
- Techmer ES Electrablend® PC 05004 FR Stainless Steel Filled
- 3M Scotch-Seal™ 2084 Metal Sealant
- 3M 8891 Bond Breaker Tape
- BASF Ultradur B 4406 G4 BKQ113 7110 20% Glass Filled PBT
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304L, 30% Cold Rolled (UNS S30403)
Copyright © lookpolymers.com All Rights Reserved