Lehmann & Voss LUVOCOM® 1850/CF/15/TF/10/EM PBT, with carbon fiber, PTFE, easy flowing
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1850/CF/15/TF/10/EM PBT, with carbon fiber, PTFE, easy flowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Electrically conductive, suitable for continuous discharging of statically generated electricity.Strong, stiff parts.Parts for electric and electronic industry, antistatic body partsInformation provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | |
| Melt Flow | 50.05 g/10 min @Load 5.00 kg, Temperature 250 °C |
50.05 g/10 min @Load 11.0 lb, Temperature 482 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 125 MPa | 18100 psi | |
| Elongation at Yield | 1.8 % | 1.8 % | |
| 2.4 % | 2.4 % | flexural | |
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | |
| Flexural Strength | 200 MPa | 29000 psi | |
| Flexural Modulus | 10.0 GPa | 1450 ksi | |
| Charpy Impact Unnotched | 3.20 J/cm² | 15.2 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| 180 °C | 356 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | mass temp |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | |
| Zone 1 | 240 - 260 °C | 464 - 500 °F | |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 28800 sec |
176 °F @Time 6.00 - 8.00 hour |
Vacuum Dryer |
| 120 °C @Time 14400 - 21600 sec |
248 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- MV Labs LA700 La(NO3)3·6H2O Lanthanum nitrate hexahydrate
- MV Labs PD430 (NH4)2PdCl6 Ammonium hexachloropalladate(IV)
- Lehmann & Voss LUVOCOM® 1106-8088/RD Polyether imide, unreinforced, laser markable
- Solvay Chemicals Potassium Fluoroaluminate
- Solvay Specialty Polymers Polymist® XPP 515-S Polytetrafluoroethylene (PTFE)
- Sumitomo Bakelite North America 73-70-70 C-P /73-70-70 VO-P Short-Glass Reinforced Diallyl Phthalate
- A. Schulman POLYBATCH™ Redwood 10416U Concentrate Based In LLDPE
- ChevronTexaco HiPerSYN™ ISO 150 Oil
- AlphaGary Evoprene™ G 3462 SEBS Thermoplastic Elastomer
- Total Xsene® XS10 YS HDPE, pipe
Copyright © lookpolymers.com All Rights Reserved