Lehmann & Voss LUVOCOM® 1106-7743 Polyether imide, with PTFE

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer Lehmann & Voss & Co.
Trade Name LUVOCOM®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lehmann & Voss LUVOCOM® 1106-7743 Polyether imide, with PTFE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Lehmann & Voss & Co.KG
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ISO 1183
Water Absorption <= 0.30 %
<= 0.30 %
23°C/24h
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Stress 90.0 MPa
13100 psi
Elongation at Yield 6.0 %
6.0 %
8.0 %
8.0 %
flexural
Modulus of Elasticity 3.00 GPa
435 ksi
Flexural Strength 130 MPa
18900 psi
Flexural Modulus 2.50 GPa
363 ksi
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
edgewise; ISO 179 1eU
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 170 °C
338 °F
Electrical Properties Metric English Comments
Insulation Resistance >= 1.00e+12 ohm
>= 1.00e+12 ohm
Processing Properties Metric English Comments
Processing Temperature 380 °C
716 °F
mass temp
Nozzle Temperature 350 - 400 °C
662 - 752 °F
Zone 1 330 - 350 °C
626 - 662 °F
Zone 2 340 - 390 °C
644 - 734 °F
Zone 3 350 - 400 °C
662 - 752 °F
Mold Temperature 150 - 180 °C
302 - 356 °F
Drying Temperature 120 °C

@Time >=28800 sec
248 °F

@Time >=8.00 hour
Dehumidifying dryer
150 °C

@Time >=14400 sec
302 °F

@Time >=4.00 hour
or
Descriptive Properties Value Comments
Color ivory