Lehmann & Voss LUVOCOM® 1105/XCF/40 PEEK, with carbon fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105/XCF/40 PEEK, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 320 MPa | 46400 psi | |
| Elongation at Yield | 1.4 % | 1.4 % | |
| 1.7 % | 1.7 % | flexural | |
| Modulus of Elasticity | 40.0 GPa | 5800 ksi | |
| Flexural Strength | 445 MPa | 64500 psi | |
| Flexural Modulus | 34.0 GPa | 4930 ksi | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 300 °C | 572 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 330 °C | 626 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Nye Lubricants 723S-MS (RL) Rheolube Grease
- PolyOne Geon™ 120 Series 121AR Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Kraton® D1118 E (SBS) Diblock Copolymer
- SABIC Innovative Plastics LNP STAT-KON DD0009P PC
- Wellman Wellamid® GS1861-N1(PTFE) Nylon 66, 35% Glass Sphere Reinforced, Enhanced Lubrication
- Tra-Con Tra-Bond 2208 Water White High Temperature Epoxy Adhesive
- Zotefoams Plastazote® LD24FM Low Density Polyethylene Foam, Flame Retarded
- Eagle Brass 110 EPT COPPER, 3/4 Hard
- 3M Scotch® 372 Performance Box Sealing Tape
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 3.0 PHR MBTS
Copyright © lookpolymers.com All Rights Reserved