Lehmann & Voss LUVOCOM® 1104-7452 Polyether ketone, with glass fiber, easy flowing
| Category | Polymer , Thermoplastic , Polyketone |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1104-7452 Polyether ketone, with glass fiber, easy flowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, mechanical- and precision engineering.Improved strength and stiffnes at elevated temperatures.Improved fatigue properties.Thermic, mechanic and chemical highly stressed parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 180 MPa | 26100 psi | |
| Elongation at Yield | 2.1 % | 2.1 % | |
| 2.7 % | 2.7 % | flexural | |
| Modulus of Elasticity | 11.5 GPa | 1670 ksi | |
| Flexural Strength | 260 MPa | 37700 psi | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | |
| Coefficient of Friction, Static | 0.28 | 0.28 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 22.0 µm/m-°C | 12.2 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| 290 °C | 554 °F | short term | |
| Vicat Softening Point | 325 °C | 617 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 390 - 420 °C | 734 - 788 °F | |
| Zone 1 | 370 - 390 °C | 698 - 734 °F | |
| Zone 2 | 380 - 420 °C | 716 - 788 °F | |
| Zone 3 | 390 - 420 °C | 734 - 788 °F | |
| Mold Temperature | 180 - 230 °C | 356 - 446 °F | |
| Drying Temperature | 140 °C @Time 14400 - 57600 sec |
284 °F @Time 4.00 - 16.0 hour |
Dehumidifying dryer |
| 150 °C @Time 14400 - 28800 sec |
302 °F @Time 4.00 - 8.00 hour |
Air-Circulation Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF15020 PD1 NBR PP, Glass Fiber-Reinforced, Chemically Coupled
- Michelman® Release Coat® 30 Water based release coating
- SABIC Innovative Plastics LNP STAT-KON REP349 PA 66
- SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly
- ChevronTexaco Delo® Extended Life Coolant System, Extender
- Arlon 56586R026 0.027" (0.686 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- AlphaGary Evoprene™ GC 5682 SEBS Thermoplastic Elastomer
- AdvanSource Biomaterials ChronoFlex® C 55D Biodurable Medical Grade Polyurethane
- Eurotec® Tecomid® NB40 NL E PA6, unfilled, natural
- Overview of materials for Polycarbonate, Glass Fiber & Bead Filled
Copyright © lookpolymers.com All Rights Reserved