Lavergne VYPET VNT 835 PET 35% Glass-Mineral Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass/Mineral Reinforced
Manufacturer Lavergne Performance Compounds
Trade Name VYPET
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lavergne VYPET VNT 835 PET 35% Glass-Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vypet VNT 835 is a 35% mineral and fiberglass reinforced PET injection molding compound designed for structural applications.Features: High temperature performance; Low warp; Excellent dimensional stabilityTypical Applications: Grill retainers; Lamp holdersInformation provided by Bieglo Gmbh for Lavergne Performance Compounds
Physical Properties Metric English Comments
Density 1.56 g/cc
0.0564 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Thickness 2.00 mm
0.0040 in/in

@Thickness 0.0787 in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Thickness 2.00 mm
0.0080 in/in

@Thickness 0.0787 in
ASTM D955
Ash 35 %
35 %
ASTM D2854
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
5 mm/min; ASTM D638
Flexural Strength 185 MPa
26800 psi
1.3 mm/min; ASTM D790
Flexural Modulus 9.90 GPa
1440 ksi
1.3 mm/min; ASTM D790
Izod Impact, Notched 0.750 J/cm

@Temperature 23.0 °C
1.41 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 213 °C
415 °F
ASTM D648
Processing Properties Metric English Comments
Feed Temperature 260 - 270 °C
500 - 518 °F
Middle Barrel Temperature 265 - 275 °C
509 - 527 °F
Front Barrel Temperature 270 - 295 °C
518 - 563 °F
Nozzle Temperature 275 - 300 °C
527 - 572 °F
Melt Temperature 275 - 300 °C
527 - 572 °F
Mold Temperature 95.0 - 120 °C
203 - 248 °F
Injection Pressure 55.0 - 85.0 MPa
7980 - 12300 psi