Lavergne VYPET 2130 Polyester Alloy Resin, 30% Fiberglass Reinforced

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified
Manufacturer	Lavergne Performance Compounds
Trade Name	VYPET
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lavergne VYPET 2130 Polyester Alloy Resin, 30% Fiberglass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Vypet 2130 is a 30% fiberglass reinforced, toughened Modified PBT injection molding compound designed for structural and electrical applications.Features: High temperature performances; Excellent dimensional stabilityTypical Applications: Appliances handles; Spotlight; Electrical componentsInformation provided by Bieglo Gmbh for Lavergne Performance Compounds

Physical Properties	Metric	English	Comments
Density	1.52 g/cc	0.0549 lb/inÂ³	ASTM D792

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	123 MPa	17800 psi	5 mm/min; ASTM D638
Elongation at Break	3.6 %	3.6 %	5 mm/min; ASTM D638
Flexural Strength	182 MPa	26400 psi	1.3 mm/min; ASTM D790
Flexural Modulus	8.00 GPa	1160 ksi	1.3 mm/min; ASTM D790
Izod Impact, Notched	0.843 J/cm @Temperature 23.0 Â°C	1.58 ft-lb/in @Temperature 73.4 Â°F	ASTM D256

Processing Properties	Metric	English
Feed Temperature	245 - 260 Â°C	473 - 500 Â°F
Middle Barrel Temperature	250 - 265 Â°C	482 - 509 Â°F
Front Barrel Temperature	255 - 270 Â°C	491 - 518 Â°F
Nozzle Temperature	260 - 270 Â°C	500 - 518 Â°F
Melt Temperature	255 - 270 Â°C	491 - 518 Â°F
Mold Temperature	65.0 - 90.0 Â°C	149 - 194 Â°F