Lanxess Pocan® KU 1-7301 000000 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer Lanxess
Trade Name Pocan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® KU 1-7301 000000 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, non-reinforced, injection molding, food contact
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Water Absorption 0.50 %
0.50 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 105 cm³/g
105 cm³/g
Viscosity number; ISO 307, 1157, 1628
Melt Flow 78 g/10 min

@Load 2.16 kg,
Temperature 260 °C
78 g/10 min

@Load 4.76 lb,
Temperature 500 °F
Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
ISO 527-1/-2
Elongation at Break 20 %
20 %
Nominal; ISO 527-1/-2
Elongation at Yield 8.0 %
8.0 %
ISO 527-1/-2
Tensile Modulus 2.70 GPa
392 ksi
ISO 527-1/-2
Charpy Impact Unnotched 15.0 J/cm²

@Temperature -30.0 °C
71.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
22.0 J/cm²

@Temperature 23.0 °C
105 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
<= 4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1 hour 2400 MPa
348000 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 1400 MPa
203000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 120 µm/m-°C
66.7 µin/in-°F
ISO 11359-1/-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75-1/-2
Vicat Softening Point 180 °C
356 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
IEC 60695-11-10
HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
Oxygen Index 24 %
24 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
IEC 60250
3.4

@Frequency 100 Hz
3.4

@Frequency 100 Hz
IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243-1
Dissipation Factor 0.0015

@Frequency 100 Hz
0.0015

@Frequency 100 Hz
IEC 60250
0.019

@Frequency 1.00e+6 Hz
0.019

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 10724
Descriptive Properties Value Comments
Additives Release agent
Form Pellets
ISO Shortname ISO 7792-1-PBT,GR,09-030
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America