Lanxess Pocan® B 3233 HR 000000 Polybutylene Terephthalate, 30% Glass Fibers

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Pocan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® B 3233 HR 000000 Polybutylene Terephthalate, 30% Glass Fibers.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, 30% glass fibers, injection molding, improved flowability, hydrolysis stabilized
Physical Properties Metric English Comments
Specific Gravity 1.48 g/cc
1.48 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Thickness 2.00 mm
 0.0030 in/in

@Thickness 0.0787 in
 Mold Temp 80°C; Melt Temp 260°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Thickness 2.00 mm
 0.010 in/in

@Thickness 0.0787 in
 Mold Temp 80°C; Melt Temp 260°C; 600 bar; ISO 294-4
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 volumetric flow - cm<sup>3</sup>/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
ISO 527-1,-2
Elongation at Break 3.0 %
3.0 %
ISO 527-1,-2
Tensile Modulus 9.00 GPa
1310 ksi
ISO 527-1,-2
Flexural Strength 200 MPa

@Strain 3.20 %
 29000 psi

@Strain 3.20 %
 ISO 178
Flexural Modulus 9.10 GPa
1320 ksi
ISO 178
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) 55.0 kJ/m²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
55.0 kJ/m²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
Charpy Impact Unnotched 6.50 J/cm²
30.9 ft-lb/in²
ISO 179-1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C
16.7 µin/in-°F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 140 µm/m-°C
77.8 µin/in-°F
ISO 11359-1,-2
Melting Point 225 °C
437 °F
ISO 11357-1,-3
Deflection Temperature at 1.8 MPa (264 psi) 206 °C
403 °F
ISO 75-1,-2
Glow Wire Test 800 °C

@Diameter 0.800 mm
 1470 °F

@Diameter 0.0315 in
 GWFI; IEC 60695-2-12
800 °C

@Diameter 1.50 mm
 1470 °F

@Diameter 0.0591 in
 GWFI; IEC 60695-2-12
800 °C

@Diameter 3.00 mm
 1470 °F

@Diameter 0.118 in
 GWFI; IEC 60695-2-12
825 °C

@Diameter 0.800 mm
 1520 °F

@Diameter 0.0315 in
 GWIT; IEC 60695-2-13
825 °C

@Diameter 1.50 mm
 1520 °F

@Diameter 0.0591 in
 GWIT; IEC 60695-2-13
825 °C

@Diameter 3.00 mm
 1520 °F

@Diameter 0.118 in
 GWIT; IEC 60695-2-13
Shrinkage 0.10 %

@Temperature 120 °C,
Time 14400 sec
 0.10 %

@Temperature 248 °F,
Time 4.00 hour
 Molding Post-shrinkage; ISO 294-4
0.10 %

@Temperature 120 °C,
Time 14400 sec
 0.10 %

@Temperature 248 °F,
Time 4.00 hour
 Molding Post-shrinkage; ISO 294-4
Electrical Properties Metric English Comments
Comparative Tracking Index 450 V
450 V
Solution A, Rating; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Processing conditions for test specimens; ISO 294
250 - 270 °C
482 - 518 °F
Recommended
Mold Temperature 80.0 °C
176 °F
Processing conditions for test specimens; ISO 294
80.0 - 100 °C
176 - 212 °F
Recommended
Drying Temperature 120 °C
248 °F
Dry Time 4 - 8 hour
4 - 8 hour
Moisture Content 0.00 - 0.020 %
0.00 - 0.020 %
Residual; Acc. To Karl Fischer
Descriptive Properties Value Comments
ISO Shortname ISO 7792-1-PBT,GHMRW,09-100,GF30