Lanxess Durethan® T 40 ZS 000000 Partially aromatic polyamide
| Category | Polymer , Thermoplastic , Nylon , Nylon, Aromatic |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® T 40 ZS 000000 Partially aromatic polyamide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Partially aromatic polyamide, injection molding and extrusion grade, easy release, transparent in all wall thicknesses, isotropic shrinkage, mechanical and electrical properties largely unaffected by conditioning state
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 6.0 % | 6.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 107 cm³/g | 107 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | Conditioned; ISO 527-1/-2 |
| 110 MPa | 16000 psi | ISO 527-1/-2 | |
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527-1/-2 |
| 3.30 GPa | 479 ksi | Conditioned; ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
IEC 60695-11-10 |
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
IEC 60695-11-10 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | Conditioned; IEC 60093 | |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 4.3 @Frequency 100 Hz |
4.3 @Frequency 100 Hz |
IEC 60250 | |
| 4.6 @Frequency 100 Hz |
4.6 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1 |
| 28.0 kV/mm | 711 kV/in | Conditioned; IEC 60243-1 | |
| Dissipation Factor | 0.040 @Frequency 100 Hz |
0.040 @Frequency 100 Hz |
IEC 60250 |
| 0.048 @Frequency 100 Hz |
0.048 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| 0.090 @Frequency 1.00e+6 Hz |
0.090 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.11 @Frequency 1.00e+6 Hz |
0.11 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6I,GTR,12-030 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |