Lanxess Durethan® DP BKV 60 H2.0 EF 900116 Nylon 6, 60% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® DP BKV 60 H2.0 EF 900116 Nylon 6, 60% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, injection molding grade, 60% glass fibers, low viscosity, good flowability (Easy Flow), good heat-resistanceApplication Examples: gearbox housings, spring holders, automotive door handles
Physical Properties Metric English Comments
Density 1.70 g/cc
0.0614 lb/in³
ISO 1183
Water Absorption 3.6 %
3.6 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 1.1 %
1.1 %
23°C/50% R.H.; Test Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0019 cm/cm
0.0019 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0047 cm/cm
0.0047 in/in
ISO 294-4, 2577
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 270 °C
15 g/10 min

@Load 11.0 lb,
Temperature 518 °F
Calculated from MVR using melt density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
Conditioned; ISO 527-1/-2
227 MPa
32900 psi
ISO 527-1/-2
Elongation at Break 2.4 %
2.4 %
ISO 527-1/-2
3.1 %
3.1 %
Conditioned; ISO 527-1/-2
Tensile Modulus 13.1 GPa
1900 ksi
Conditioned; ISO 527-1/-2
20.4 GPa
2960 ksi
ISO 527-1/-2
Charpy Impact Unnotched 8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eU
9.00 J/cm²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
9.00 J/cm²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eU
9.50 J/cm²

@Temperature -30.0 °C
45.2 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 1.70 J/cm²

@Temperature 23.0 °C
8.09 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
1.80 J/cm²

@Temperature -30.0 °C
8.57 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C
5.56 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C
44.4 µin/in-°F
ISO 11359-1/-2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 212 °C
414 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 190 °C
374 °F
ISO 75-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 8.00e+11 ohm-cm
8.00e+11 ohm-cm
Conditioned; IEC 60093
5.80e+14 ohm-cm
5.80e+14 ohm-cm
IEC 60093
Dielectric Constant 4.7

@Frequency 1.00e+6 Hz
4.7

@Frequency 1.00e+6 Hz
IEC 60250
5.1

@Frequency 1.00e+6 Hz
5.1

@Frequency 1.00e+6 Hz
Conditioned; IEC 60250
5.3

@Frequency 100 Hz
5.3

@Frequency 100 Hz
IEC 60250
11.2

@Frequency 100 Hz
11.2

@Frequency 100 Hz
Conditioned; IEC 60250
Dielectric Strength 33.0 kV/mm
838 kV/in
IEC 60243-1
33.0 kV/mm
838 kV/in
Conditioned; IEC 60243-1
Dissipation Factor 0.0164

@Frequency 100 Hz
0.0164

@Frequency 100 Hz
IEC 60250
0.0177

@Frequency 1.00e+6 Hz
0.0177

@Frequency 1.00e+6 Hz
IEC 60250
0.0651

@Frequency 1.00e+6 Hz
0.0651

@Frequency 1.00e+6 Hz
Conditioned; IEC 60250
0.2149

@Frequency 100 Hz
0.2149

@Frequency 100 Hz
Conditioned; IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Form Pellets
ISO Shortname ISO1874-PA6, MHR, 10-190, GF60
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America