Lanxess DurethanÂ® DP BKV 30 XF 000000 Nylon 6, 30% Glass Fiber

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	Lanxess
Trade Name	Durethan®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lanxess DurethanÂ® DP BKV 30 XF 000000 Nylon 6, 30% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PA 6, 30% glass fibers, injection molding, improved flowability, improved surface finishInformation provided by LANXESS.

Physical Properties	Metric	English	Comments
Specific Gravity	1.34 g/cc	1.34 g/cc	ISO 1183
Bulk Density	0.600 g/cc	0.0217 lb/inÂ³	ISO 60
Linear Mold Shrinkage, Flow	0.00030 cm/cm	0.00030 in/in	Post-shrinkage, 60x60x2; 120Â°C; 4 hour; ISO 294-4
	0.0022 cm/cm	0.0022 in/in	60x60x2; 270Â°C / WZ 80Â°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse	0.00090 cm/cm	0.00090 in/in	Post-shrinkage, 60x60x2; 120Â°C; 4 hour; ISO 294-4
	0.0053 cm/cm	0.0053 in/in	60x60x2; 270Â°C / WZ 80Â°C; 600 bar; ISO 294-4
Melt Flow	28 g/10 min @Load 5.00 kg, Temperature 260 Â°C	28 g/10 min @Load 11.0 lb, Temperature 500 Â°F	ISO 1133-1

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	155 MPa	22500 psi	ISO 2039-1
Tensile Strength at Break	95.0 MPa	13800 psi	cond.; ISO 527-1, -2; 5 mm/min
	165 MPa	23900 psi	d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break	3.0 %	3.0 %	d.a.m.; ISO 527-1, -2; 5 mm/min
	5.0 %	5.0 %	cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus	5.50 GPa	798 ksi	cond.; ISO 527-1, -2; 1 mm/min
	8.60 GPa	1250 ksi	d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength	150 MPa @Strain 5.80 %	21800 psi @Strain 5.80 %	cond., 2 mm/min; ISO 178-A
	240 MPa @Strain 3.80 %	34800 psi @Strain 3.80 %	d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength	130 MPa @Strain 3.50 %	18900 psi @Strain 3.50 %	cond., 2 mm/min; ISO 178-A
	235 MPa @Strain 3.50 %	34100 psi @Strain 3.50 %	d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus	4.90 GPa	711 ksi	cond., 2 mm/min; ISO 178-A
	7.50 GPa	1090 ksi	d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO)	12.0 kJ/mÂ²	5.71 ft-lb/inÂ²	d.a.m.; ISO 180-1A
	15.0 kJ/mÂ²	7.14 ft-lb/inÂ²	cond.; ISO 180-1A
Izod Impact, Unnotched (ISO)	60.0 kJ/mÂ² @Temperature -30.0 Â°C	28.6 ft-lb/inÂ² @Temperature -22.0 Â°F	d.a.m.; ISO 180-1U
	60.0 kJ/mÂ² @Temperature -30.0 Â°C	28.6 ft-lb/inÂ² @Temperature -22.0 Â°F	cond.; ISO 180-1U
	70.0 kJ/mÂ² @Temperature 23.0 Â°C	33.3 ft-lb/inÂ² @Temperature 73.4 Â°F	d.a.m.; ISO 180-1U
	70.0 kJ/mÂ² @Temperature 23.0 Â°C	33.3 ft-lb/inÂ² @Temperature 73.4 Â°F	cond.; ISO 180-1U
Charpy Impact Unnotched	9.00 J/cmÂ²	42.8 ft-lb/inÂ²	d.a.m.; ISO 179-1eU
	9.00 J/cmÂ²	42.8 ft-lb/inÂ²	cond.; ISO 179-1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 Âµm/m-Â°C @Temperature 23.0 - 55.0 Â°C	11.1 Âµin/in-Â°F @Temperature 73.4 - 131 Â°F	ISO 11359-1, -2
CTE, linear, Transverse to Flow	110 Âµm/m-Â°C @Temperature 23.0 - 55.0 Â°C	61.1 Âµin/in-Â°F @Temperature 73.4 - 131 Â°F	ISO 11359-1, -2
Melting Point	220 Â°C	428 Â°F	10Â°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi)	210 Â°C	410 Â°F	ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi)	165 Â°C	329 Â°F	ISO 75-1, -2

Processing Properties	Metric	English	Comments
Melt Temperature	250 - 290 Â°C	482 - 554 Â°F
	270 Â°C	518 Â°F	for test specimens; ISO 294
Mold Temperature	80.0 Â°C	176 Â°F	for test specimens; ISO 294
	80.0 - 120 Â°C	176 - 248 Â°F
Drying Temperature	80.0 Â°C	176 Â°F
Dry Time	2 - 6 hour	2 - 6 hour
Moisture Content	0.030 - 0.12 %	0.030 - 0.12 %	residual; Karl Fischer Test

Descriptive Properties	Value	Comments
ISO Shortname	ISO 1874 PA 6, GR, 10-090, GF30