Lanxess Durethan® DP BKV 240 H2.0 901510 Copolyamide, 40% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP BKV 240 H2.0 901510 Copolyamide, 40% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CoPA, injection molding grade, 40% glass fibers reinforced, elastomer-modified, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0027 cm/cm | 0.0027 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0074 cm/cm | 0.0074 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Conditioned; ISO 527-1/-2 |
| 150 MPa | 21800 psi | ISO 527-1/-2 | |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 |
| 7.5 % | 7.5 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 5.70 GPa | 827 ksi | Conditioned; ISO 527-1/-2 |
| 10.5 GPa | 1520 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 1247 | 1247 | Puncture maximum force (N); ISO 6603-2 |
| 1065 @Temperature -30.0 °C |
1065 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 8.00 J | 5.90 ft-lb | ISO 6603-2 |
| 4.70 J @Temperature -30.0 °C |
3.47 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 4.70 J @Temperature -30.0 °C |
3.47 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 140 µm/m-°C | 77.8 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 210 °C | 410 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 125 °C | 257 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | High impact or high impact modified | |
| Form | Pellets | |
| ISO Shortname | ISO1874-PA6/66-HI, MHR, -110, GF40 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 10 FRG 5 Polyamide 6, 10% Glass Fiber, Flame Retardant
- LyondellBasell Petrothene® XL07425 Copolymer
- LG Chemical 60HR HIPS
- SABIC Innovative Plastics LNP THERMOCOMP WH0245A PBT (Asia Pacific)
- Dow Corning Q2-5057 Fluid
- Epoxy Technology EPO-TEK® 337H Graphite-Filled, High Temperature Epoxy
- DuPont Performance Polymers Zytel® 74G33J NC010 Nylon 66 (Unverified Data**)
- Esstech X-167-0470 Glass Ionomer Cement Liquid
- Bulk Molding Compounds BMC HT12-1026 Unsaturated Polyester Bulk Molding Compound
- ExxonMobil Oppalyte™ 30MD447 OPP Film
Copyright © lookpolymers.com All Rights Reserved