Lanxess Durethan® DP BC 500 H2.0 901510 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP BC 500 H2.0 901510 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, extrusion and blow molding grade, non-reinforced, elastomer-modified, high viscosity, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Water Absorption | 9.4 % | 9.4 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0013 cm/cm | 0.0013 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0014 cm/cm | 0.0014 in/in | ISO 294-4, 2577 |
| Melt Flow | 40 g/10 min @Load 10.0 kg, Temperature 300 °C |
40 g/10 min @Load 22.0 lb, Temperature 572 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | Conditioned; ISO 527-1/-2 |
| 75.0 MPa | 10900 psi | ISO 527-1/-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 |
| 28 % | 28 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 0.750 GPa | 109 ksi | Conditioned; ISO 527-1/-2 |
| 2.70 GPa | 392 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 22.0 J/cm² @Temperature -30.0 °C |
105 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 15.0 J/cm² @Temperature 23.0 °C |
71.4 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,EHS,18-030 | |
| Processing | Blow molding | |
| Other extrusion | ||
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- DSM Yparex® 8104 R Polyolefin Adhesive Resin (European Grade) (discontinued **)
- Momentive Performance Materials Siloprenâ„¢ LSR 3486/35 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
- SABIC Innovative Plastics NORYL GTX GTX674PC PPE+PA6
- CeramTec Sonox® P5 Piezoceramic
- Plenco 7200 Phenolic, Granular, Injection Molded
- Eifeler Coatings Technology SISTRAL® AlTiN PVD Coating
- Cytec (Conap) RN-1000 / EA-02 Conapoxy® Resin / Conacure® Hardener
- DuPont Performance Polymers Zytel® ST801A NC010A Nylon 66 (Unverified Data**)
- Beijing Evergrow Resources UHF-F150 UHMW PE Fiber
Copyright © lookpolymers.com All Rights Reserved