Lanxess Durethan® DP 1801/30 H3.0 000000 Nylon 6, 30% Milled Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® DP 1801/30 H3.0 000000 Nylon 6, 30% Milled Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, injection molding grade, 30% milled fibers, UL 94V-2 at 0.8 mm, max. temperature in glow wire test: 960 °C at 0,75 mm, "halogen-free", good heat-ageing resistanceApplication Examples: Medical Appliance Housings
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 5.9 %
5.9 %
Test Sim. to ISO 62
Viscosity Test 104 cm³/g
104 cm³/g
Viscosity number; ISO 307, 1157, 1628
Linear Mold Shrinkage, Flow 0.0055 cm/cm
0.0055 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0063 cm/cm
0.0063 in/in
ISO 294-4, 2577
Melt Flow 38 g/10 min

@Load 5.00 kg,
Temperature 260 °C
38 g/10 min

@Load 11.0 lb,
Temperature 500 °F
Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa
6820 psi
Conditioned; ISO 527-1/-2
93.0 MPa
13500 psi
ISO 527-1/-2
Tensile Strength, Yield 50.0 MPa
7250 psi
Conditioned; ISO 527-1/-2
96.0 MPa
13900 psi
ISO 527-1/-2
Elongation at Break 4.0 %
4.0 %
ISO 527-1/-2
28 %
28 %
Conditioned; ISO 527-1/-2
Elongation at Yield 2.4 %
2.4 %
ISO 527-1/-2
9.7 %
9.7 %
Conditioned; ISO 527-1/-2
Tensile Modulus 3.40 GPa
493 ksi
Conditioned; ISO 527-1/-2
7.60 GPa
1100 ksi
ISO 527-1/-2
Charpy Impact Unnotched 5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
8.40 J/cm²

@Temperature 23.0 °C
40.0 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature -30.0 °C
<= 4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
<= 1.00 J/cm²

@Temperature 23.0 °C
<= 4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 82.0 µm/m-°C
45.6 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 35.0 µm/m-°C
19.4 µin/in-°F
ISO 11359-1/-2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
ISO 75-1/-2
Flammability, UL94 V-2

@Thickness 0.800 mm
V-2

@Thickness 0.0315 in
IEC 60695-11-10
V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
IEC 60695-11-10
Oxygen Index 30 %
30 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Dielectric Strength 38.0 kV/mm
965 kV/in
IEC 60243-1
Comparative Tracking Index 550 V
550 V
IEC 60112
Descriptive Properties Value Comments
Additives Flame retarding agent
Lubricants
Features Flame retardant
Heat stabilized or stable to heat
Form Pellets
ISO Shortname ISO 1874-PA 6,MFH,14-080,GF30; ISO 1043-PA GF FR(30)