Lanxess Durethan® CI 31 F 000000 Copolyamide PA6/6I

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® CI 31 F 000000 Copolyamide PA6/6I.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Copolyamide PA6/6I, low melt point (188-191°C), low viscosity, no additives, very high transparency, in compliance with FDA as far as the PA-layer is separated from the food by a 50 µm PE film
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Water Absorption 10 %
10 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 3.0 %
3.0 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 133 cm³/g
133 cm³/g
Viscosity number; ISO 307, 1157, 1628
Melt Flow 28 g/10 min

@Load 5.00 kg,
Temperature 260 °C
28 g/10 min

@Load 11.0 lb,
Temperature 500 °F
Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 80.0 MPa
11600 psi
ISO 527-1/-2
Elongation at Break 250 %
250 %
ISO 527-1/-2
Elongation at Yield 4.5 %
4.5 %
ISO 527-1/-2
Tensile Modulus 2.40 GPa
348 ksi
ISO 527-1/-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
Melting Point 188 °C
370 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 54.0 °C
129 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75-1/-2
Descriptive Properties Value Comments
Form Pellets
ISO Shortname ISO 1874: PA 6/ 6I,FNT,14-020
Processing Film extrusion
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America