Lanxess Durethan® BKV 50 H2.0 901510 Nylon 6, 50% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 50 H2.0 901510 Nylon 6, 50% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, injection molding grade, 50% glass fibers, good heat-ageing resistance
Physical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
ISO 1183
Water Absorption 5.0 %
5.0 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 140 cm³/g
140 cm³/g
Viscosity number; ISO 307, 1157, 1628
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
Conditioned; ISO 527-1/-2
220 MPa
31900 psi
ISO 527-1/-2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
5.0 %
5.0 %
Conditioned; ISO 527-1/-2
Tensile Modulus 9.80 GPa
1420 ksi
Conditioned; ISO 527-1/-2
16.3 GPa
2360 ksi
ISO 527-1/-2
Charpy Impact Unnotched 8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 179/1eU
9.00 J/cm²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.30 J/cm²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 Conditioned; ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
2.50 J/cm²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
 Conditioned; ISO 179/1eA
Impact 1207
1207
Puncture maximum force (N); ISO 6603-2
1060

@Temperature -30.0 °C
 1060

@Temperature -22.0 °F
 Puncture maximum force (N); ISO 6603-2
Puncture Energy 4.20 J
3.10 ft-lb
ISO 6603-2
8.90 J
6.56 ft-lb
Conditioned; ISO 6603-2
3.70 J

@Temperature -30.0 °C
 2.73 ft-lb

@Temperature -22.0 °F
 ISO 6603-2
3.70 J

@Temperature -30.0 °C
 2.73 ft-lb

@Temperature -22.0 °F
 Conditioned; ISO 6603-2
Tensile Creep Modulus, 1 hour 8100 MPa
1.17e+6 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 6600 MPa
957000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C
38.9 µin/in-°F
ISO 11359-1/-2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 175 °C
347 °F
ISO 75-1/-2
Vicat Softening Point 200 °C
392 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 IEC 60695-11-10
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 IEC 60695-11-10
Oxygen Index 24 %
24 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Comparative Tracking Index 550 V
550 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Features Heat stabilized or stable to heat
Form Pellets
ISO Shortname ISO 1874-PA 6,MHR,14-140,GF50
Processing Injection molding