Lanxess Durethan® BKV 315 Z H2.0 901510 Nylon 6, 15% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 315 Z H2.0 901510 Nylon 6, 15% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6 extrusion- and blow molding-grade with 15% glass fibers, branched/structural viscosity, elastomer-modified, good heat-ageing resistance, dry-impact modifiedApplication Examples: air intake hoses, thermoformed covers
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0087 cm/cm
0.0087 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0056 cm/cm
0.0056 in/in
ISO 294-4, 2577
Melt Flow 4 g/10 min

@Load 5.00 kg,
Temperature 270 °C
4 g/10 min

@Load 11.0 lb,
Temperature 518 °F
Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Conditioned; ISO 527-1/-2
105 MPa
15200 psi
ISO 527-1/-2
Tensile Strength, Yield 60.0 MPa
8700 psi
Conditioned; ISO 527-1/-2
105 MPa
15200 psi
ISO 527-1/-2
Elongation at Break 5.0 %
5.0 %
ISO 527-1/-2
19 %
19 %
Conditioned; ISO 527-1/-2
Elongation at Yield 3.5 %
3.5 %
ISO 527-1/-2
11 %
11 %
Conditioned; ISO 527-1/-2
Tensile Modulus 2.50 GPa
363 ksi
Conditioned; ISO 527-1/-2
5.40 GPa
783 ksi
ISO 527-1/-2
Charpy Impact Unnotched 7.00 J/cm²

@Temperature -30.0 °C
33.3 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
7.00 J/cm²

@Temperature 23.0 °C
33.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eU
10.0 J/cm²

@Temperature 23.0 °C
47.6 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
3.00 J/cm²

@Temperature 23.0 °C
14.3 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eA
Impact 1200
1200
Puncture maximum force (N); ISO 6603-2
630

@Temperature -30.0 °C
630

@Temperature -22.0 °F
Puncture maximum force (N); ISO 6603-2
Puncture Energy 4.90 J
3.61 ft-lb
ISO 6603-2
2.50 J

@Temperature -30.0 °C
1.84 ft-lb

@Temperature -22.0 °F
ISO 6603-2
2.50 J

@Temperature -30.0 °C
1.84 ft-lb

@Temperature -22.0 °F
Conditioned; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C
33.3 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 130 µm/m-°C
72.2 µin/in-°F
ISO 11359-1/-2
Melting Point 219 °C
426 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 55.0 °C
131 °F
ISO 75-1/-2
Vicat Softening Point 205 °C
401 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
IEC 60695-11-10
Electrical Properties Metric English Comments
Comparative Tracking Index 375 V
375 V
IEC 60112
Descriptive Properties Value Comments
Form Pellets
ISO Shortname ISO 1874-PA 6-HI,EH,22-050,GF15
Processing Blow molding
Other extrusion
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America
Users viewing this material also viewed the following: