- Lanxess Durethan® BKV 20 FN00 000000 Nylon 6, 18% Glass Fiber
Lanxess Durethan® BKV 20 FN00 000000 Nylon 6, 18% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 20 FN00 000000 Nylon 6, 18% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA6, injection molding grade, 18% glass fibers, UL94 V-0 at 0,75 mm ( in house test), free of halogen and red phosphorus, specially for electro/electronic applications in regard to IEC60335-1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.345 g/cc | 0.04859 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0034 cm/cm | 0.0034 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0064 cm/cm | 0.0064 in/in | ISO 294-4, 2577 |
| Melt Flow | 17 g/10 min @Load 2.16 kg, Temperature 260 °C |
17 g/10 min @Load 4.76 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Conditioned; ISO 527-1/-2 |
| 110 MPa | 16000 psi | ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| 3.4 % | 3.4 % | Nominal; ISO 527-1/-2 | |
| 4.5 % | 4.5 % | Nominal, Conditioned; ISO 527-1/-2 | |
| 4.9 % | 4.9 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 4.50 GPa | 653 ksi | Conditioned; ISO 527-1/-2 |
| 7.96 GPa | 1150 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
IEC 60695-11-10 |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 575 V | 575 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MFR,-080,GF20 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Braskem Flexus® 9210 LLDPE Blown Film Extrusion (discontinued **)
- MRC Polymers NAXELLâ„¢ PC110-20G General Purpose Polycarbonate, Medium Viscosity, 20% Glass Fiber
- Teknor Apex APEX® 3301-90 Polyvinyl Chloride, Flexible
- Teknor Apex APEX® 80-C118Q Polyvinyl Chloride, Flexible
- Beijing Chemical Industry KAIFA® 301-G30RF PBT Resin
- Azoty Tarnow™ Tarnamid® T-27 GF15 Polyamide 6 - Glass Fiber Reinforced
- Plastcom SLOVALEN PH 73 T 20 PP, 20% mineral filling
- E-Polymers EFLEX® I2010 Ionomer
- Bhansali Engineering Abstron HR-105 ABS Super Heat Resistant
Copyright © lookpolymers.com All Rights Reserved