Lanxess Durethan® BKV 15 H.3 DUS008 000000 Nylon 6, 15% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Heat Stabilized
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 15 H.3 DUS008 000000 Nylon 6, 15% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 15% glass fibers, injection molding, heat-ageing stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Density 1.228 g/cc
0.04436 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0035 cm/cm
0.0035 in/in
150x105x3, 280°C / MT 80°C; 500 bar; ISO 2577
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
150x105x3, 280°C / MT 80°C; 500 bar; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
conditioned, 5 mm/min; ISO 527-1,-2
130 MPa
18900 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 3.0 %
3.0 %
5 mm/min; ISO 527-1,-2
12 %
12 %
conditioned, 5 mm/min; ISO 527-1,-2
Tensile Modulus 3.10 GPa
450 ksi
conditioned, 1 mm/min; ISO 527-1,-2
6.50 GPa
943 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 110 MPa
16000 psi
conditioned, 2 mm/min; ISO 178-A
205 MPa
29700 psi
2 mm/min; ISO 178-A
Flexural Modulus 3.10 GPa
450 ksi
conditioned, 2 mm/min; ISO 178-A
5.50 GPa
798 ksi
2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
10.0 kJ/m²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 180-1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
40.0 kJ/m²

@Temperature -30.0 °C
 19.0 ft-lb/in²

@Temperature -22.0 °F
 conditioned; ISO 180-1U
45.0 kJ/m²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
85.0 kJ/m²

@Temperature 23.0 °C
 40.4 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 180-1U
Charpy Impact Unnotched 4.50 J/cm²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
4.50 J/cm²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 conditioned; ISO 179-1eU
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 179-1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 16.7 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2
Melting Point 220 °C
428 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ISO 75-1,-2
Shrinkage 0.150 %

@Temperature 120 °C,
Time 14400 sec
 0.150 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, 150x105x3; ISO 2577
0.150 %

@Temperature 120 °C,
Time 14400 sec
 0.150 %

@Temperature 248 °F,
Time 4.00 hour
 post-shrinkage, transverse, 150x105x3; ISO 2577
Processing Properties Metric English Comments
Melt Temperature 280 °C
536 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 2.00 - 6.00 hour

@Temperature 80.0 °C
 2.00 - 6.00 hour

@Temperature 176 °F
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer test