Lanxess Durethan® BKV 140 H2.0 900051 Copolyamide, 40% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 140 H2.0 900051 Copolyamide, 40% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CoPA, injection molding grade, 40% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 40, even in the dry state, good heat-ageing resistance
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Water Absorption 6.0 %
6.0 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 1.6 %
1.6 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 134 cm³/g
134 cm³/g
Viscosity number; ISO 307, 1157, 1628
Melt Flow 7 g/10 min

@Load 5.00 kg,
Temperature 260 °C
7 g/10 min

@Load 11.0 lb,
Temperature 500 °F
Estimated using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa
16700 psi
Conditioned; ISO 527-1/-2
180 MPa
26100 psi
ISO 527-1/-2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
6.0 %
6.0 %
Conditioned; ISO 527-1/-2
Tensile Modulus 6.70 GPa
972 ksi
Conditioned; ISO 527-1/-2
11.5 GPa
1670 ksi
ISO 527-1/-2
Charpy Impact Unnotched 8.50 J/cm²

@Temperature -30.0 °C
40.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
8.50 J/cm²

@Temperature -30.0 °C
40.4 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eU
9.00 J/cm²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
11.0 J/cm²

@Temperature 23.0 °C
52.3 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Conditioned; ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
3.50 J/cm²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
Conditioned; ISO 179/1eA
Impact 1144
1144
Puncture maximum force (N); ISO 6603-2
921

@Temperature -30.0 °C
921

@Temperature -22.0 °F
Puncture maximum force (N); ISO 6603-2
Puncture Energy 4.00 J
2.95 ft-lb
ISO 6603-2
3.00 J

@Temperature -30.0 °C
2.21 ft-lb

@Temperature -22.0 °F
ISO 6603-2
3.00 J

@Temperature -30.0 °C
2.21 ft-lb

@Temperature -22.0 °F
Conditioned; ISO 6603-2
Tensile Creep Modulus, 1 hour 6100 MPa
885000 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 4900 MPa
711000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
Melting Point 213 °C
415 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
Vicat Softening Point 200 °C
392 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
IEC 60695-11-10
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
IEC 60695-11-10
Oxygen Index 22 %
22 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm
1.00e+11 ohm-cm
Conditioned; IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
4.0

@Frequency 1.00e+6 Hz
IEC 60250
4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250
5.0

@Frequency 1.00e+6 Hz
5.0

@Frequency 1.00e+6 Hz
Conditioned; IEC 60250
10

@Frequency 100 Hz
10

@Frequency 100 Hz
Conditioned; IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
Conditioned; IEC 60243-1
40.0 kV/mm
1020 kV/in
IEC 60243-1
Comparative Tracking Index 500 V
500 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Features Heat stabilized or stable to heat
High impact or high impact modified
Form Pellets
ISO Shortname ISO 1874-PA 6/66-I, MHR, 14-110, GF40
Processing Injection molding