Lanxess Durethan® BC 700 HTS DUSXBL 900116 Nylon 6, Impact Modified

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BC 700 HTS DUSXBL 900116 Nylon 6, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, non-reinforced, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.027 g/cc
1.027 g/cc
ISO 1183
Moisture Absorption at Equilibrium 1.9 %
1.9 %
50% RH; ISO 62
Water Absorption at Saturation 8.1 %
8.1 %
ISO 62
Mechanical Properties Metric English Comments
Tensile Strength, Yield 28.0 MPa
4060 psi
d.a.m.; ISO 527-1, -2; 50 mm/min
Elongation at Yield 6.5 %
6.5 %
d.a.m.; ISO 527-1, -2; 50 mm/min
Tensile Modulus 0.210 GPa
30.5 ksi
cond.; ISO 527-1, -2; 1 mm/min
0.980 GPa
142 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 12.0 MPa

@Strain 9.00 %
 1740 psi

@Strain 9.00 %
 cond., 2 mm/min; ISO 178-A
35.0 MPa

@Strain 6.10 %
 5080 psi

@Strain 6.10 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 7.00 MPa

@Strain 3.50 %
 1020 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
30.0 MPa

@Strain 3.50 %
 4350 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 0.230 GPa
33.4 ksi
cond., 2 mm/min; ISO 178-A
0.980 GPa
142 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 70.0 kJ/m²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1A
90.0 kJ/m²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 cond.; ISO 180-1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 cond.; ISO 179-1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
Charpy Impact, Notched 7.50 J/cm²

@Temperature -30.0 °C
 35.7 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
10.5 J/cm²

@Temperature 23.0 °C
 50.0 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
Puncture Energy 50.0 J

@Load <=336 kg,
Temperature 23.0 °C
 36.9 ft-lb

@Load <=742 lb,
Temperature 73.4 °F
 ISO 6603-2
50.0 J

@Load <=418 kg,
Temperature -30.0 °C
 36.9 ft-lb

@Load <=922 lb,
Temperature -22.0 °F
 ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 200 µm/m-°C

@Temperature 23.0 - 55.0 °C
 111 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 200 µm/m-°C

@Temperature 23.0 - 55.0 °C
 111 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 212 °C
414 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 53.0 °C
127 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Melt Temperature 230 - 280 °C
446 - 536 °F
270 °C
518 °F
for test specimens; ISO 294
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
80.0 °C
176 °F
for test specimens; ISO 294
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.00 - 0.060 %
0.00 - 0.060 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6/66-HI, BHS, 14-010