Lanxess Durethan® AKV 50 H3.0 000000 Nylon 66, 50% Glass Fibers

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® AKV 50 H3.0 000000 Nylon 66, 50% Glass Fibers.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66, 50% glass fibers, injection molding, heat-ageing stabilized
Physical Properties Metric English Comments
Specific Gravity 1.57 g/cc
1.57 g/cc
ISO 1183
Bulk Density 0.700 g/cc
0.0253 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Thickness 2.00 mm
 0.0040 in/in

@Thickness 0.0787 in
 Mold Temp 80°C; Melt Temp 300°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Thickness 2.00 mm
 0.010 in/in

@Thickness 0.0787 in
 Mold Temp 80°C; Melt Temp 300°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 220 MPa
31900 psi
ISO 527-1,-2
Elongation at Break 2.5 %
2.5 %
ISO 527-1,-2
Tensile Modulus 15.2 GPa
2200 ksi
ISO 527-1,-2
Flexural Strength 360 MPa

@Strain 3.00 %
 52200 psi

@Strain 3.00 %
 ISO 178
Flexural Modulus 14.0 GPa
2030 ksi
ISO 178
Izod Impact, Notched (ISO) 13.0 kJ/m²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
15.0 kJ/m²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Izod Impact, Unnotched (ISO) 90.0 kJ/m²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1U
90.0 kJ/m²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1U
Charpy Impact Unnotched 10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
10.0 J/cm²

@Temperature -30.0 °C
 47.6 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
Charpy Impact, Notched 1.40 J/cm²

@Temperature -40.0 °C
 6.66 ft-lb/in²

@Temperature -40.0 °F
 ISO 179-1eA
1.50 J/cm²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
1.70 J/cm²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
Melting Point 262 °C
504 °F
ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75-1,-2
Shrinkage 0.10 %

@Temperature 120 °C,
Time 14400 sec
 0.10 %

@Temperature 248 °F,
Time 4.00 hour
 Molding Post-shrinkage; ISO 294-4
0.10 %

@Temperature 120 °C,
Time 14400 sec
 0.10 %

@Temperature 248 °F,
Time 4.00 hour
 Molding Post-shrinkage; ISO 294-4
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Dielectric Constant 4.4

@Frequency 1.00e+6 Hz
 4.4

@Frequency 1.00e+6 Hz
 IEC 60250
5.0

@Frequency 100 Hz
 5.0

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 38.0 kV/mm

@Thickness 1.00 mm
 965 kV/in

@Thickness 0.0394 in
 IEC 60243-1
Dissipation Factor 0.023

@Frequency 1.00e+6 Hz
 0.023

@Frequency 1.00e+6 Hz
 IEC 60250
0.025

@Frequency 100 Hz
 0.025

@Frequency 100 Hz
 IEC 60250
Comparative Tracking Index 500 V
500 V
Solution A, Rating; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 290 °C
554 °F
Processing conditions for test specimens; ISO 294
280 - 300 °C
536 - 572 °F
Recommended
Mold Temperature 80.0 °C
176 °F
Processing conditions for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Recommended
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
Residual; Acc. To Karl Fischer
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 66,GHR,14-160,GF50