Lanxess Durethan® AC 30 DUS027 000000 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade , Nylon 66, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AC 30 DUS027 000000 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, non-reinforced, injection molded, impact modifiedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.111 g/cc | 0.04014 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | at yield, conditioned, 50 mm/min; ISO 527-1,-2 |
| 70.0 MPa | 10200 psi | at yield, 50 mm/min; ISO 527-1,-2 | |
| Elongation at Break | 18 % | 18 % | 50 mm/min; ISO 527-1,-2 |
| 75 % | 75 % | conditioned, 50 mm/min; ISO 527-1,-2 | |
| Elongation at Yield | 5.8 % | 5.8 % | ISO 527-1,-2 |
| 25 % | 25 % | conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 1.10 GPa | 160 ksi | conditioned, 1 mm/min; ISO 527-1,-2 |
| 3.00 GPa | 435 ksi | 1 mm/min; ISO 527-1,-2 | |
| Flexural Strength | 40.0 MPa | 5800 psi | conditioned, 2 mm/min; ISO 178-A |
| 100 MPa | 14500 psi | 2 mm/min; ISO 178-A | |
| Flexural Modulus | 1.00 GPa | 145 ksi | conditioned, 2 mm/min; ISO 178-A |
| 2.60 GPa | 377 ksi | 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 180-1A | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
conditioned; ISO 179-1eA | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Melting Point | 261 °C | 502 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C | 378 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ISO 75-1,-2 |
| Shrinkage | 0.200 % @Temperature 120 °C, Time 14400 sec |
0.200 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, 60x60x2; ISO 294-4 |
| 0.200 % @Temperature 120 °C, Time 14400 sec |
0.200 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, transverse, 60x60x2; ISO 294-4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 2.00 - 6.00 hour @Temperature 80.0 °C |
2.00 - 6.00 hour @Temperature 176 °F |
|
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer test |