Lanxess Durethan® A 30 H3.0 000000 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® A 30 H3.0 000000 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, non reinforced, injection molding, heat-ageing stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 2.8 % | 2.8 % | 50%RH; ISO 62 |
| Water Absorption at Saturation | 8.5 % | 8.5 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 2.00 mm |
0.0080 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm @Thickness 2.00 mm |
0.019 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Conditioned; ISO 527-1,-2 |
| 95.0 MPa | 13800 psi | ISO 527-1,-2 | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal, Conditioned; ISO 527-1,-2 |
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527-1,-2 |
| 20 % | 20 % | Conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 1.30 GPa | 189 ksi | Conditioned; ISO 527-1,-2 |
| 3.50 GPa | 508 ksi | ISO 527-1,-2 | |
| Flexural Strength | 50.0 MPa @Strain 8.00 % |
7250 psi @Strain 8.00 % |
Conditioned; ISO 178 |
| 130 MPa @Strain 6.00 % |
18900 psi @Strain 6.00 % |
ISO 178 | |
| Flexural Yield Strength | 40.0 MPa @Strain 3.50 % |
5800 psi @Strain 3.50 % |
Conditioned; ISO 178 |
| 105 MPa @Strain 3.50 % |
15200 psi @Strain 3.50 % |
ISO 178 | |
| Flexural Modulus | 1.20 GPa | 174 ksi | Conditioned; ISO 178 |
| 3.10 GPa | 450 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
Conditioned; ISO 180-1A | |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eU | |
| 16.0 J/cm² @Temperature 23.0 °C |
76.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| 19.0 J/cm² @Temperature 23.0 °C |
90.4 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
Conditioned; ISO 179-1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1,-2 |
| Melting Point | 261 °C | 502 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1,-2 |
| Vicat Softening Point | >= 230 °C @Load 5.10 kg |
>= 446 °F @Load 11.2 lb |
ISO 306 |
| Glow Wire Test | 750 °C @Diameter 2.00 mm |
1380 °F @Diameter 0.0787 in |
IEC 60695-2-12 |
| Shrinkage | 0.20 % @Temperature 120 °C, Time 14400 sec |
0.20 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| 0.40 % @Temperature 120 °C, Time 14400 sec |
0.40 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | Conditioned; IEC 60093 |
| 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 | |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |
| 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 13 @Frequency 100 Hz |
13 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 25.0 kV/mm @Thickness 1.00 mm |
635 kV/in @Thickness 0.0394 in |
Conditioned; IEC 60243-1 |
| 31.0 kV/mm @Thickness 1.00 mm |
787 kV/in @Thickness 0.0394 in |
IEC 60243-1 | |
| Dissipation Factor | 0.012 @Frequency 100 Hz |
0.012 @Frequency 100 Hz |
IEC 60250 |
| 0.057 @Frequency 1.00e+6 Hz |
0.057 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.10 @Frequency 1.00e+6 Hz |
0.10 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.32 @Frequency 100 Hz |
0.32 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Solution A, Rating; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 °C | 536 °F | Processing conditions for test specimens; ISO 294 |
| 275 - 295 °C | 527 - 563 °F | Recommended | |
| Mold Temperature | 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 |
| 80.0 - 100 °C | 176 - 212 °F | Recommended | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | Residual; Acc. To Karl Fischer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 66,GHR,14-030 |
Users viewing this material also viewed the following:
- Poco Graphite Glassmate® GM Graphite
- SABIC PP681K Polypropylene Random Copolymer for Injection Molding
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N774 Filler
- LG Chemical LUCEL MR-320 Low Warpage POM, 20% Mineral Filled
- Stellarchem MP-8001 TPE Compound
- Teknor Apex APEX® 90-A529C-72 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics Valox® SHF4930 PBT (Europe-Africa-Middle East)
- ChevronTexaco ISO 68 Ultra Gear Lubricant
- Aremco Corr-Paint™ CP4000 High Temperature Protective Silicone Coating, Metal Oxide Filled
- ATI Allegheny Ludlum Stainless Steel AL 904L™ Alloy (UNS N08904)
Copyright © lookpolymers.com All Rights Reserved