LNP Thermocomp® UF-1006 A HS Polyphthalamide, Glass Fiber Reinforcement (discontinued **)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LNP Thermocomp® UF-1006 A HS Polyphthalamide, Glass Fiber Reinforcement
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Heat StabilizedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | Method A; ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | at 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 183 MPa | 26500 psi | ASTM D638 |
| Tensile Strength, Yield | 183 MPa | 26500 psi | ASTM D638 |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D638 |
| Elongation at Yield | 1.9 % | 1.9 % | ASTM D638 |
| Tensile Modulus | 11.6 GPa | 1680 ksi | ASTM D638 |
| Flexural Strength | 248 MPa | 36000 psi | ASTM D790 |
| Flexural Modulus | 11.5 GPa | 1670 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 3.18 mm |
1.30 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 4.11 J/cm @Thickness 3.18 mm |
7.70 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Notched (ISO) | 7.10 kJ/m² | 3.38 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 30.5 kJ/m² | 14.5 ft-lb/in² | ISO 180 |
| Falling Dart Impact | 9.93 J | 7.32 ft-lb | ASTM D3763 |
| Impact Test | 1.48 J | 1.09 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 282 °C | 540 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 329 °C | 601 - 624 °F | |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.15 % | 0.15 % | Suggested |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi |