LNP Thermocomp® STN-F-1006 HS Polyamide 46, Glass Fiber Reinforcement (discontinued **)

Category	Polymer , Thermoplastic , Nylon , Nylon 46
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LNP Thermocomp® STN-F-1006 HS Polyamide 46, Glass Fiber Reinforcement (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: Heat StabilizedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

Physical Properties	Metric	English	Comments
Specific Gravity	1.40 g/cc	1.40 g/cc	Method A; ASTM D792
Water Absorption	1.3 %	1.3 %	at 24 hrs; ASTM D570
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.014 cm/cm	0.014 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	190 MPa	27600 psi	ASTM D638
Tensile Strength, Yield	190 MPa	27600 psi	ASTM D638
Elongation at Break	3.3 %	3.3 %	ASTM D638
Elongation at Yield	3.3 %	3.3 %	ASTM D638
Tensile Modulus	11.1 GPa	1610 ksi	ASTM D638
Flexural Strength	296 MPa	42900 psi	ASTM D790
Flexural Modulus	9.63 GPa	1400 ksi	ASTM D790
Izod Impact, Notched	0.907 J/cm @Thickness 3.18 mm	1.70 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	11.5 J/cm @Thickness 3.18 mm	21.5 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Notched (ISO)	9.20 kJ/m²	4.38 ft-lb/in²	ISO 180
Izod Impact, Unnotched (ISO)	70.2 kJ/m²	33.4 ft-lb/in²	ISO 180
Falling Dart Impact	12.0 J	8.85 ft-lb	ASTM D3763
Impact Test	3.29 J	2.43 ft-lb	Multi-Axial Instrumented Impact Energy; ISO 6603-2

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	289 °C	552 °F	Unannealed; ASTM D648

Processing Properties	Metric	English	Comments
Melt Temperature	310 - 321 °C	590 - 610 °F
Mold Temperature	82.2 - 121 °C	180 - 250 °F
Drying Temperature	82.2 °C	180 °F
Dry Time	4 hour	4 hour
Moisture Content	0.20 %	0.20 %	Suggested
Back Pressure	0.172 - 0.345 MPa	24.9 - 50.0 psi

Users viewing this material also viewed the following: