LNP Thermocomp® QF-1006 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® QF-1006 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
Method A; ASTM D792
Water Absorption 0.20 %
0.20 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
ASTM D638
Tensile Strength, Yield 150 MPa
21800 psi
ASTM D638
Elongation at Break 3.6 %
3.6 %
ASTM D638
Elongation at Yield 3.6 %
3.6 %
ASTM D638
Tensile Modulus 8.41 GPa
1220 ksi
ASTM D638
Flexural Strength 248 MPa
36000 psi
ASTM D790
Flexural Modulus 7.86 GPa
1140 ksi
ASTM D790
Izod Impact, Notched 1.23 J/cm

@Thickness 3.18 mm
2.30 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 11.2 J/cm

@Thickness 3.18 mm
21.0 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 9.70 kJ/m²
4.62 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 71.8 kJ/m²
34.2 ft-lb/in²
ISO 180
Falling Dart Impact 9.93 J
7.32 ft-lb
ASTM D3763
Impact Test 2.72 J
2.01 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 31.0 µm/m-°C

@Temperature 20.0 °C
17.2 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature 20.0 °C
40.0 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 221 °C
430 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 268 - 274 °C
514 - 525 °F
Mold Temperature 82.2 - 93.3 °C
180 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4 hour
4 hour
Moisture Content 0.020 %
0.020 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi