LNP Thermocomp® LF-1003 Polyetheretherketone, Glass Fiber Reinforcement (discontinued **)

Category	Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LNP Thermocomp® LF-1003 Polyetheretherketone, Glass Fiber Reinforcement (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	130 MPa	18900 psi	ASTM D638
Elongation at Break	6.0 %	6.0 %	ASTM D638
Izod Impact, Notched	0.694 J/cm @Thickness 3.18 mm	1.30 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	7.47 J/cm @Thickness 3.18 mm	14.0 ft-lb/in @Thickness 0.125 in	ASTM D256

Processing Properties	Metric	English	Comments
Melt Temperature	379 - 388 °C	714 - 730 °F
Mold Temperature	135 - 163 °C	275 - 325 °F
Drying Temperature	121 - 149 °C	250 - 300 °F
Dry Time	4 hour	4 hour
Moisture Content	0.10 %	0.10 %	Suggested
Back Pressure	0.345 - 0.689 MPa	50.0 - 99.9 psi