LNP Thermocomp® LC-1006 EM Polyetheretherketone, Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® LC-1006 EM Polyetheretherketone, Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.41 g/cc
1.41 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 228 MPa
33100 psi
ASTM D638
Tensile Strength, Yield 228 MPa
33100 psi
ASTM D638
Elongation at Break 1.3 %
1.3 %
ASTM D638
Elongation at Yield 1.3 %
1.3 %
ASTM D638
Tensile Modulus 25.0 GPa
3630 ksi
ASTM D638
Flexural Strength 338 MPa
49000 psi
ASTM D790
Flexural Modulus 21.6 GPa
3130 ksi
ASTM D790
Izod Impact, Notched 0.641 J/cm

@Thickness 3.18 mm
1.20 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 4.32 J/cm

@Thickness 3.18 mm
8.09 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 37.4 kJ/m²
17.8 ft-lb/in²
ISO 180
Falling Dart Impact 7.62 J
5.62 ft-lb
ASTM D3763
Impact Test 4.57 J
3.37 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 18.0 µm/m-°C

@Temperature 20.0 °C
10.0 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 32.0 µm/m-°C

@Temperature 20.0 °C
17.8 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 300 °C
572 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 379 - 388 °C
714 - 730 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.10 %
0.10 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi