LNP Thermocomp® FP-VC-1003 BK8-019 Polyvinylidene Fluoride, Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), with Carbon Fiber
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® FP-VC-1003 BK8-019 Polyvinylidene Fluoride, Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.76 g/cc
1.76 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.013 cm/cm
0.010 - 0.013 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 77.9 MPa
11300 psi
ASTM D638
Tensile Strength, Yield 77.9 MPa
11300 psi
ASTM D638
Elongation at Break 0.80 %
0.80 %
ASTM D638
Elongation at Yield 0.80 %
0.80 %
ASTM D638
Tensile Modulus 14.3 GPa
2070 ksi
ASTM D638
Flexural Strength 124 MPa
18000 psi
ASTM D790
Flexural Modulus 11.8 GPa
1710 ksi
ASTM D790
Izod Impact, Notched 0.587 J/cm

@Thickness 3.18 mm
1.10 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 2.03 J/cm

@Thickness 3.18 mm
3.80 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 14.6 kJ/m²
6.95 ft-lb/in²
ISO 180
Falling Dart Impact 11.4 J
8.41 ft-lb
ASTM D3763
Impact Test 3.01 J
2.22 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 31.0 µm/m-°C

@Temperature 20.0 °C
17.2 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 85.0 µm/m-°C

@Temperature 20.0 °C
47.2 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 166 °C
331 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 159 °C
318 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 218 - 232 °C
424 - 450 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi
Descriptive Properties Value Comments
Color Black