LNP Thermocomp® FP-EC-1004 Ethylene Tetrafluoroethylene Copolymer, Carbon Fiber Reinforcement  (discontinued *

Category Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® FP-EC-1004 Ethylene Tetrafluoroethylene Copolymer, Carbon Fiber Reinforcement  (discontinued *.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.75 g/cc
1.75 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0070 cm/cm
0.0070 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.022 cm/cm
0.022 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
ASTM D638
Elongation at Break 2.5 %
2.5 %
ASTM D638
Tensile Modulus 13.3 GPa
1930 ksi
ASTM D638
Flexural Strength 103 MPa
14900 psi
ASTM D790
Flexural Modulus 10.5 GPa
1520 ksi
ASTM D790
Izod Impact, Notched 1.81 J/cm

@Thickness 3.18 mm
3.39 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 5.87 J/cm

@Thickness 3.18 mm
11.0 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 15.4 kJ/m²
7.33 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 36.8 kJ/m²
17.5 ft-lb/in²
ISO 180
Falling Dart Impact 14.0 J
10.3 ft-lb
ASTM D3763
Impact Test 6.00 J
4.43 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 25.0 µm/m-°C

@Temperature 20.0 °C
13.9 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
CTE, linear, Transverse to Flow 54.0 µm/m-°C

@Temperature 20.0 °C
30.0 µin/in-°F

@Temperature 68.0 °F
TMA; ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 253 °C
487 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 209 °C
408 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 316 °C
601 °F
Mold Temperature 93.3 - 121 °C
200 - 250 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi