LNP Thermocomp® EF-1006 BK8-114 Polyetherimide, Glass Fiber Reinforcement (discontinued **)

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LNP Thermocomp® EF-1006 BK8-114 Polyetherimide, Glass Fiber Reinforcement (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.

Physical Properties	Metric	English	Comments
Specific Gravity	1.52 g/cc	1.52 g/cc	Method A; ASTM D792
Water Absorption	0.10 %	0.10 %	at 24 hrs; ASTM D570
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0050 cm/cm	0.0050 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	188 MPa	27300 psi	ASTM D638
Tensile Strength, Yield	188 MPa	27300 psi	ASTM D638
Elongation at Break	2.4 %	2.4 %	ASTM D638
Elongation at Yield	2.4 %	2.4 %	ASTM D638
Tensile Modulus	11.4 GPa	1650 ksi	ASTM D638
Flexural Strength	269 MPa	39000 psi	ASTM D790
Flexural Modulus	11.4 GPa	1650 ksi	ASTM D790
Izod Impact, Notched (ISO)	10.5 kJ/m²	5.00 ft-lb/in²	ISO 180
Izod Impact, Unnotched (ISO)	48.7 kJ/m²	23.2 ft-lb/in²	ISO 180
Falling Dart Impact	12.4 J	9.15 ft-lb	ASTM D3763
Impact Test	2.64 J	1.95 ft-lb	Multi-Axial Instrumented Impact Energy; ISO 6603-2
Coefficient of Friction, Dynamic	0.55	0.55	vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static	0.50	0.50	vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor	262 x 10^-8 mm³/N-M	130 x 10^-10 in³-min/ft-lb-hr	40psi, 50ft/min; tested in accordance with LNP WI-0687

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	204 °C	399 °F	Unannealed; ASTM D648

Processing Properties	Metric	English	Comments
Melt Temperature	360 - 366 °C	680 - 691 °F
Mold Temperature	121 - 149 °C	250 - 300 °F
Drying Temperature	121 - 149 °C	250 - 300 °F
Dry Time	4 hour	4 hour
Moisture Content	0.020 %	0.020 %	Suggested
Back Pressure	0.345 - 0.689 MPa	50.0 - 99.9 psi

Descriptive Properties	Value	Comments
Color	Black